颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 | ||
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0010 cm/cm | 0.00050 - 0.0010 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.0025 - 0.0030 cm/cm | 0.0025 - 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 205 MPa | 29700 psi | 5mm/min; ISO 527-2/1A | ||
| 237 MPa | 34400 psi | ASTM D638 | |||
| 106 MPa @Temperature 121 °C |
15400 psi @Temperature 250 °F |
ASTM D638 | |||
| 281 MPa @Temperature -40.0 °C |
40800 psi @Temperature -40.0 °F |
ASTM D638 | |||
| Elongation at Break | 2.11 % | 2.11 % | 5mm/min; ISO 527-2/1A | ||
| 2.5 % @Temperature 22.8 °C |
2.5 % @Temperature 73.0 °F |
ASTM D638 | |||
| 2.6 % @Temperature -40.0 °C |
2.6 % @Temperature -40.0 °F |
ASTM D638 | |||
| 3.0 % @Temperature 121 °C |
3.0 % @Temperature 250 °F |
ASTM D638 | |||
| Tensile Modulus | 12.4 GPa | 1800 ksi | 1mm/min; ISO 527-2/1A | ||
| 7.31 GPa @Temperature 121 °C |
1060 ksi @Temperature 250 °F |
ASTM D638 | |||
| 11.8 GPa @Temperature -40.0 °C |
1710 ksi @Temperature -40.0 °F |
ASTM D638 | |||
| 13.4 GPa @Temperature 22.8 °C |
1950 ksi @Temperature 73.0 °F |
ASTM D638 | |||
| Flexural Strength | 335 MPa | 48600 psi | ISO 178 | ||
| 339 MPa | 49100 psi | ASTM D790 | |||
| 159 MPa @Temperature 121 °C |
23000 psi @Temperature 250 °F |
ASTM D790 | |||
| 398.2 MPa @Temperature -40.0 °C |
57750 psi @Temperature -40.0 °F |
ASTM D790 | |||
| Flexural Modulus | 11.15 GPa | 1617 ksi | ISO 178 | ||
| 6.07 GPa @Temperature 121 °C |
880 ksi @Temperature 250 °F |
ASTM D790 | |||
| 11.8 GPa @Temperature 22.8 °C |
1710 ksi @Temperature 73.0 °F |
ASTM D790 | |||
| 12.5 GPa @Temperature -40.0 °C |
1810 ksi @Temperature -40.0 °F |
ASTM D790 | |||
| Izod Impact, Notched | 3.68 J/cm | 6.90 ft-lb/in | ASTM D256 | ||
| 3.04 J/cm @Temperature -40.0 °C |
5.70 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |||
| 5.13 J/cm @Temperature 121 °C |
9.60 ft-lb/in @Temperature 250 °F |
ASTM D256 | |||
| Charpy Impact, Notched | 3.20 J/cm² | 15.2 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1, -2 | ||
| 210 °C | 410 °F | ASTM D648 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| 80.0 - 100 °C | 176 - 212 °F | Cavity temperature | |||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 265 - 275 °C | 509 - 527 °F | |||
| Zone 2 | 270 - 275 °C | 518 - 527 °F | |||
| Zone 3 | 275 - 280 °C | 527 - 536 °F | |||
| Zone 4 | 275 - 280 °C | 527 - 536 °F | |||
| Die Temperature | 275 - 280 °C | 527 - 536 °F | |||
| Melt Temperature | 270 - 285 °C | 518 - 545 °F | |||
| Mold Temperature | 85.0 - 95.0 °C | 185 - 203 °F | |||
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | 0.18 % | 0.18 % | Necessary low maximum residual | ||
| Dew Point | <= -30.0 °C | <= -22.0 °F | Pre-drying | ||
| De |
|||||
| Injection molding | Yes | ||||
| Longer pre-drying times/storage | Material can be over dried and may discolor. | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。