| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.00450 - 0.00600 cm/cm | 0.00450 - 0.00600 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.00650 - 0.00900 cm/cm | 0.00650 - 0.00900 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 65.0 MPa | 9430 psi | |||
| Elongation at Break | 2.50 % | 2.50 % | |||
| Tensile Modulus | 6.10 GPa | 885 ksi | |||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | 1.00e+9 ohm | 1.00e+9 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | |||
| Vicat Softening Point | 145 °C @Load 5.00 kg |
293 °F @Load 11.0 lb |
|||
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|||
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
||||
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |||
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
|||
| De |
|||||
| ISO Shrinkage - Pressure | 60 MPa | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。