颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.40 % | 2.40 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 170 MPa | 24700 psi | cond; ISO 527-1/-2 |
| 260 MPa | 37700 psi | dry; ISO 527-1/-2 | |
| 95.0 MPa @Temperature 200 °C |
13800 psi @Temperature 392 °F |
ISO 527-1/-2 | |
| 105 MPa @Temperature 180 °C |
15200 psi @Temperature 356 °F |
ISO 527-1/-2 | |
| 115 MPa @Temperature 160 °C |
16700 psi @Temperature 320 °F |
ISO 527-1/-2 | |
| 140 MPa @Temperature 120 °C |
20300 psi @Temperature 248 °F |
ISO 527-1/-2 | |
| Elongation at Break | 1.7 % | 1.7 % | dry; ISO 527-1/-2 |
| 3.5 % | 3.5 % | cond; ISO 527-1/-2 | |
| 3.1 % @Temperature 120 °C |
3.1 % @Temperature 248 °F |
ISO 527-1/-2 | |
| 3.1 % @Temperature 160 °C |
3.1 % @Temperature 320 °F |
ISO 527-1/-2 | |
| 3.1 % @Temperature 180 °C |
3.1 % @Temperature 356 °F |
ISO 527-1/-2 | |
| 3.1 % @Temperature 200 °C |
3.1 % @Temperature 392 °F |
ISO 527-1/-2 | |
| Tensile Modulus | 14.5 GPa | 2100 ksi | cond; ISO 527-1/-2 |
| 24.0 GPa | 3480 ksi | dry; ISO 527-1/-2 | |
| 11.0 GPa @Temperature 200 °C |
1600 ksi @Temperature 392 °F |
ISO 527-1/-2 | |
| 11.5 GPa @Temperature 180 °C |
1670 ksi @Temperature 356 °F |
ISO 527-1/-2 | |
| 12.0 GPa @Temperature 160 °C |
1740 ksi @Temperature 320 °F |
ISO 527-1/-2 | |
| 13.5 GPa @Temperature 120 °C |
1960 ksi @Temperature 248 °F |
ISO 527-1/-2 | |
| Fatigue Strength | 67.0 MPa @# of Cycles 1.00e+7 , Temperature 140 °C |
9720 psi @# of Cycles 1.00e+7 , Temperature 284 °F |
R = 0.1, 8 Hz, dry |
| 76.0 MPa @# of Cycles 1.00e+6 , Temperature 140 °C |
11000 psi @# of Cycles 1.00e+6 , Temperature 284 °F |
R = 0.1, 8 Hz, dry | |
| 86.0 MPa @# of Cycles 100000 , Temperature 140 °C |
12500 psi @# of Cycles 100000 , Temperature 284 °F |
R = 0.1, 8 Hz, dry | |
| 97.0 MPa @# of Cycles 10000 , Temperature 140 °C |
14100 psi @# of Cycles 10000 , Temperature 284 °F |
R = 0.1, 8 Hz, dry | |
| 110 MPa @# of Cycles 1000 , Temperature 140 °C |
16000 psi @# of Cycles 1000 , Temperature 284 °F |
R = 0.1, 8 Hz, dry | |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.70 J/cm² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | dry; ISO 75-1/-2 |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。