PA46 TS300 PA46 无筋、_产品资讯

PA46 TS300 具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.18 g/cc	0.0426 lb/in³	dry; ISO 1183
Moisture Absorption	3.70 %	3.70 %	Sim. To ISO 62
Linear Mold Shrinkage, Flow	0.020 cm/cm	0.020 in/in	Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse	0.020 cm/cm	0.020 in/in	Sim. To ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	55.0 MPa	7980 psi	cond; ISO 527-1/-2
	100 MPa	14500 psi	dry; ISO 527-1/-2
	30.0 MPa @Temperature 200 °C	4350 psi @Temperature 392 °F	ISO 527-1/-2
	35.0 MPa @Temperature 180 °C	5080 psi @Temperature 356 °F	ISO 527-1/-2
	40.0 MPa @Temperature 160 °C	5800 psi @Temperature 320 °F	ISO 527-1/-2
	50.0 MPa @Temperature 120 °C	7250 psi @Temperature 248 °F	ISO 527-1/-2
Elongation at Break	40 %	40 %	dry; ISO 527-1/-2
	>= 50 %	>= 50 %	cond; ISO 527-1/-2
	>= 50 % @Temperature 120 °C	>= 50 % @Temperature 248 °F	ISO 527-1/-2
	>= 50 % @Temperature 160 °C	>= 50 % @Temperature 320 °F	ISO 527-1/-2
	>= 50 % @Temperature 180 °C	>= 50 % @Temperature 356 °F	ISO 527-1/-2
	>= 50 % @Temperature 200 °C	>= 50 % @Temperature 392 °F	ISO 527-1/-2
Tensile Modulus	1.00 GPa	145 ksi	cond; ISO 527-1/-2
	3.30 GPa	479 ksi	dry; ISO 527-1/-2
	0.500 GPa @Temperature 200 °C	72.5 ksi @Temperature 392 °F	ISO 527-1/-2
	0.600 GPa @Temperature 180 °C	87.0 ksi @Temperature 356 °F	ISO 527-1/-2
	0.650 GPa @Temperature 160 °C	94.3 ksi @Temperature 320 °F	ISO 527-1/-2
	0.800 GPa @Temperature 120 °C	116 ksi @Temperature 248 °F	ISO 527-1/-2
Flexural Modulus	0.900 GPa	131 ksi	cond; ISO 178
	3.00 GPa	435 ksi	dry; ISO 178
	0.600 GPa @Temperature 160 °C	87.0 ksi @Temperature 320 °F	ISO 178
	0.800 GPa @Temperature 120 °C	116 ksi @Temperature 248 °F	ISO 178
Izod Impact Resistance	0.400 J/cm² @Temperature -40.0 °C	1.90 ft-lb/in² @Temperature -40.0 °F	cond; ISO 180/1A
	0.400 J/cm² @Temperature -40.0 °C	1.90 ft-lb/in² @Temperature -40.0 °F	dry; ISO 180/1A
	1.00 J/cm² @Temperature 23.0 °C	4.76 ft-lb/in² @Temperature 73.4 °F	dry; ISO 180/1A
	3.50 J/cm² @Temperature 23.0 °C	16.7 ft-lb/in² @Temperature 73.4 °F	cond; ISO 180/1A
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	cond; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	cond; ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	dry; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	dry; ISO 179/1eU
Charpy Impact, Notched	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	cond; ISO 179/1eA
	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eA
	1.00 J/cm² @Temperature 23.0 °C	4.76 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eA
	3.50 J/cm² @Temperature 23.0 °C	16.7 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	cond; IEC 60093
	1.00e+15 ohm-cm	1.00e+15 ohm-cm	dry; IEC 60093
Dielectric Strength	20.0 kV/mm	508 kV/in	cond; IEC 60243-1
	25.0 kV/mm	635 kV/in	dry; IEC 60243-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	85.0 µm/m-°C	47.2 µin/in-°F	dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow	110 µm/m-°C	61.1 µin/in-°F	dry; ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	190 °C	374 °F	dry; ISO 75-1/-2
Flammability, UL94	V-2 @Thickness 1.50 mm	V-2 @Thickness 0.0591 in	dry; IEC 60695-11-10
	V-2 @Thickness 0.750 mm	V-2 @Thickness 0.0295 in	dry; IEC 60695-11-10

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。

欢迎各位客户前来咨询：

联系人：夏先生

手机：13501802636

QQ ：205730283

邮箱：205730283@qq.com

PA46 TS300 PA46 无筋 、

PA46 TS300 PA46 无筋、