| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.90 % | 2.90 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | dry; ISO 527-1/-2 |
| Elongation at Break | 3.5 % | 3.5 % | dry; ISO 527-1/-2 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | dry; ISO 527-1/-2 |
| Flexural Modulus | 6.00 GPa | 870 ksi | dry; ISO 178 |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.790 mm |
HB @Thickness 0.0311 in |
dry; IEC 60695-11-10 |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。