PA46 TS200F10 PA46-GF50 、_产品资讯

PA46 TS200F10 具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.62 g/cc	0.0585 lb/in³	dry; ISO 1183
Moisture Absorption	1.85 %	1.85 %	Sim. To ISO 62
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in	Sim. To ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	160 MPa	23200 psi	cond; ISO 527-1/-2
	250 MPa	36300 psi	dry; ISO 527-1/-2
	100 MPa @Temperature 200 °C	14500 psi @Temperature 392 °F	ISO 527-1/-2
	110 MPa @Temperature 180 °C	16000 psi @Temperature 356 °F	ISO 527-1/-2
	120 MPa @Temperature 160 °C	17400 psi @Temperature 320 °F	ISO 527-1/-2
	140 MPa @Temperature 120 °C	20300 psi @Temperature 248 °F	ISO 527-1/-2
Elongation at Break	2.7 %	2.7 %	dry; ISO 527-1/-2
	5.0 %	5.0 %	cond; ISO 527-1/-2
	5.0 % @Temperature 120 °C	5.0 % @Temperature 248 °F	ISO 527-1/-2
	5.0 % @Temperature 160 °C	5.0 % @Temperature 320 °F	ISO 527-1/-2
	5.0 % @Temperature 180 °C	5.0 % @Temperature 356 °F	ISO 527-1/-2
	5.0 % @Temperature 200 °C	5.0 % @Temperature 392 °F	ISO 527-1/-2
Tensile Modulus	10.0 GPa	1450 ksi	cond; ISO 527-1/-2
	16.0 GPa	2320 ksi	dry; ISO 527-1/-2
	6.60 GPa @Temperature 200 °C	957 ksi @Temperature 392 °F	ISO 527-1/-2
	7.00 GPa @Temperature 180 °C	1020 ksi @Temperature 356 °F	ISO 527-1/-2
	7.40 GPa @Temperature 160 °C	1070 ksi @Temperature 320 °F	ISO 527-1/-2
	8.20 GPa @Temperature 120 °C	1190 ksi @Temperature 248 °F	ISO 527-1/-2
Flexural Modulus	9.00 GPa	1310 ksi	cond; ISO 178
	14.0 GPa	2030 ksi	dry; ISO 178
	6.50 GPa @Temperature 160 °C	943 ksi @Temperature 320 °F	ISO 178
	7.30 GPa @Temperature 120 °C	1060 ksi @Temperature 248 °F	ISO 178
Izod Impact Resistance	1.40 J/cm² @Temperature -40.0 °C	6.66 ft-lb/in² @Temperature -40.0 °F	cond; ISO 180/1A
	1.40 J/cm² @Temperature -40.0 °C	6.66 ft-lb/in² @Temperature -40.0 °F	dry; ISO 180/1A
	1.60 J/cm² @Temperature 23.0 °C	7.61 ft-lb/in² @Temperature 73.4 °F	dry; ISO 180/1A
	2.40 J/cm² @Temperature 23.0 °C	11.4 ft-lb/in² @Temperature 73.4 °F	cond; ISO 180/1A
Charpy Impact Unnotched	9.00 J/cm² @Temperature -30.0 °C	42.8 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eU
	10.0 J/cm² @Temperature 23.0 °C	47.6 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eU
	10.0 J/cm² @Temperature -30.0 °C	47.6 ft-lb/in² @Temperature -22.0 °F	cond; ISO 179/1eU
	11.0 J/cm² @Temperature 23.0 °C	52.3 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eU
Charpy Impact, Notched	1.40 J/cm² @Temperature -30.0 °C	6.66 ft-lb/in² @Temperature -22.0 °F	cond; ISO 179/1eA
	1.40 J/cm² @Temperature -30.0 °C	6.66 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eA
	1.60 J/cm² @Temperature 23.0 °C	7.61 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eA
	2.40 J/cm² @Temperature 23.0 °C	11.4 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	cond; IEC 60093
	1.00e+14 ohm-cm	1.00e+14 ohm-cm	dry; IEC 60093
Dielectric Strength	20.0 kV/mm	508 kV/in	cond; IEC 60243-1
	30.0 kV/mm	762 kV/in	dry; IEC 60243-1
Comparative Tracking Index	300 V	300 V	dry; IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	25.0 µm/m-°C	13.9 µin/in-°F	dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow	40.0 µm/m-°C	22.2 µin/in-°F	dry; ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	290 °C	554 °F	dry; ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	dry; IEC 60695-11-10

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。