pmma VM，阿科玛，高流动性 耐化学性 耐候性 光学性

 pmma VM 的物性表：

Physical Properties	Metric	English	Comments
Specific Gravity	1.18 g/cc	1.18 g/cc	ASTM D792
Water Absorption	0.30 %	0.30 %	weight gain after 24 hr. immersion; ASTM D570
Linear Mold Shrinkage	0.0020 - 0.0060 cm/cm	0.0020 - 0.0060 in/in	ASTM D955
Melt Flow	14.5 g/10 min @Load 3.80 kg, Temperature 230 °C	14.5 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D1238
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	89	89	ASTM D785
Tensile Strength, Ultimate	66.2 MPa	9600 psi	ASTM D638
Tensile Modulus	3.03 GPa	440 ksi	ASTM D638
Flexural Strength	<= 96.5 MPa	<= 14000 psi	ASTM D790
Flexural Modulus	3.00 GPa	435 ksi	ASTM D790
Izod Impact, Notched	0.160 J/cm	0.300 ft-lb/in	ASTM D256
Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.187 W/m-K	1.30 BTU-in/hr-ft²-°F	ASTM C177
Deflection Temperature at 0.46 MPa (66 psi)	83.3 °C	182 °F	annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	77.2 °C	171 °F	annealed; ASTM D648
Vicat Softening Point	82.2 °C	180 °F	50°C/hr; 50N; ASTM D1525
	88.3 °C	191 °F	50°C/hr; 10N; ASTM D1525
Optical Properties	Metric	English	Comments
Refractive Index	1.49 @Temperature 22.8 °C	1.49 @Temperature 73.0 °F	ND; ASTM D542
Haze	<= 2.0 % @Thickness 3.17 mm	<= 2.0 % @Thickness 0.125 in	ASTM D1003
Transmission, Visible	92 % @Thickness 3.17 mm	92 % @Thickness 0.125 in	ASTM D1003

材料说明：有机玻璃®VM是一种热塑性丙烯酸树脂注塑成型应用制定。它的特点是它非常高的熔融流动和耐化学性。有机玻璃®VM具有优良的耐候性和光学性能使其在户外应用Excel需要稳定，高质量的外观和/或精密光学。有机玻璃®VM易加工由于其优异的热稳定性，挤出的熔体强度，优良的工具表面的繁殖和释放性能。它具有优良的耐许多化学物质，包括无机酸溶液，碱，如VM和P石脑油和庚烷脂肪族碳氢化合物。此外，它几乎没有受到影响的范围广泛的商业产品，包括许多饮料，食品，洗涤剂溶液和清洁剂。