| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 | ||
| Water Absorption | 0.20 % | 0.20 % | Immersion, 24hr; ASTM D570(2) | ||
| Water Absorption at Saturation | 0.90 % | 0.90 % | Immersion; ASTM D570(2) | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 88 | 88 | ASTM D785 | ||
| Hardness, Rockwell R | 120 | 120 | ASTM D785 | ||
| Hardness, Shore D | 85 | 85 | ASTM D2240 | ||
| Tensile Strength | 65.5 MPa | 9500 psi | ASTM D638 | ||
| Elongation at Break | 30 % | 30 % | ASTM D638 | ||
| Tensile Modulus | 2.76 GPa | 400 ksi | ASTM D638 | ||
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 | ||
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 | ||
| Compressive Strength | 103 MPa | 15000 psi | 10% Def.; ASTM D695 | ||
| Compressive Modulus | 2.76 GPa | 400 ksi | ASTM D695 | ||
| Shear Strength | 55.2 MPa | 8000 psi | ASTM D732 | ||
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 Type A | ||
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | Dry vs. Steel; QTM55007 | ||
| K (wear) Factor | 403 x 10-8 mm³/N-M | 200 x 10-10 in³-min/ft-lb-hr | QTM 55010 | ||
| Limiting Pressure Velocity | 0.0946 MPa-m/sec | 2700 psi-ft/min | 4:1 safety factor; QTM 55007 | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistivity per Square | >= 1.00e+13 ohm | >= 1.00e+13 ohm | EOS/ESD S11.11 | ||
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
ASTM D150 | ||
| Dielectric Strength | 16.5 kV/mm | 420 kV/in | Short Term; ASTM D149 | ||
| Dissipation Factor | 0.0050 @Frequency 1e+6 Hz |
0.0050 @Frequency 1e+6 Hz |
ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 97.2 µm/m-°C @Temperature -40.0 - 149 °C |
54.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 | ||
| Thermal Conductivity | 0.231 W/m-K | 1.60 BTU-in/hr-ft²-°F | ASTM F433 | ||
| Melting Point | 168 °C | 335 °F | Crystalline, Peak; ASTM D3418 | ||
| Maximum Service Temperature, Air | 82.2 °C | 180 °F | Long Term | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 | ||
| Flammability, UL94 | HB | HB | 1/8 inch (Estimated Rating) | ||
| Compliance Properties | Metric | English | Comments | ||
| 3A-Dairy | Yes | Yes | |||
| Canada AG | Yes | Yes | |||
| FDA | Yes | Yes | |||
| NSF | Yes | Yes | STD 51 & 61 Natural Only | ||
| USDA | Yes | Yes | |||
| USP Class VI | No | No | |||
| Chemical Resistance Properties | Metric | English | Comments | ||
| Acids, Strong (pH 1-3) | Unacceptable | Unacceptable | |||
| Acids, Weak | Limited | Limited | |||
| Alcohols | Acceptable | Acceptable | |||
| Alkalies, Strong (pH 11-14) | Unacceptable | Unacceptable | |||
| Alkalies, Weak | Acceptable | Acceptable | |||
| Chlorinated Solvents | Limited | Limited | |||
| Conductive / Static Dissipative | No | No | |||
| Continuous Sunlight | Limited | Limited | |||
| Hot Water / Steam | Limited | Limited | |||
| Hydrocarbons - Aliphatic | Acceptable | Acceptable | |||
| Hydrocarbons - Aromatic | Acceptable | Acceptable | |||
| Inorganic Salt Solutions | Acceptable | Acceptable | |||
| Ketones, Esters | Acceptable | Acceptable | |||
| De |
|||||
| Color | Natural / Black | ||||
| Machinability | 1 | 1-10, 1=Easier to Machine |
|||
POM 的简介
聚甲醛学名聚氧化聚甲醛（简称POM） 又称赛钢、特钢。
它是以甲醛等为原料聚合所得。
POM-H（聚甲醛均聚物），POM-K（聚甲醛共聚物）是高密度、高结晶度的热塑性工程塑料。
具有良好的物理、机械和化学性能，尤其是有优异的耐摩擦性能。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。
POM 电学性能
POM的电绝缘性较好，几乎不受温度和湿度的影响；介电常数和介电损耗在很宽的温度、湿度和频率范围内变化很小；耐电弧性极好，并可在高温下保持。POM的介电强度与厚度有关，厚度0.127mm时为82.7kV/mm，厚度为1.88mm时为23.6kV/mm。
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
POM 环境性能:
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。
POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。
POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。
应用范围：
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。