巴斯夫 POM 2320 003 UNC q600_产品资讯

巴斯夫 POM 2320 003 UNC q600 的物性表：

Physical Properties	Metric	English	Comments

Density	1.40 g/cc	0.0506 lb/in³	ISO 1183
Water Absorption	0.80 %	0.80 %	ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C/50% R.H.; ISO 62
Melt Flow	11 g/10 min @Load 2.16 kg, Temperature 190 °C	11 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	145 MPa	21000 psi	358/30; ISO 2039
Tensile Strength	50.0 MPa @Time 1.81e+7 sec	7250 psi @Time 5040 hour	Storage in fuel CM15_AP at +60°C
	55.0 MPa @Time 2.59e+6 sec	7980 psi @Time 720 hour	Storage in fuel CM15_AP at +60°C
	55.0 MPa @Time 1.04e+7 sec	7980 psi @Time 2880 hour	Storage in fuel CM15_AP at +60°C
Tensile Strength, Yield	65.0 MPa	9430 psi	50mm/min; ISO 527
Elongation at Break	28 %	28 %	50mm/min; ISO 527
Elongation at Yield	9.0 %	9.0 %	50mm/min; ISO 527
Modulus of Elasticity	2.70 GPa	392 ksi	ISO 527
Izod Impact, Notched (ISO)	5.50 kJ/m² @Temperature 23.0 °C	2.62 ft-lb/in² @Temperature 73.4 °F	ISO 180/A
	5.50 kJ/m² @Temperature -30.0 °C	2.62 ft-lb/in² @Temperature -22.0 °F	ISO 180/A
Charpy Impact Unnotched	18.0 J/cm²	85.7 ft-lb/in²	ISO 179
	17.0 J/cm² @Temperature -30.0 °C	80.9 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.550 J/cm²	2.62 ft-lb/in²	ISO 179
	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 179
Tensile Creep Modulus, 1000 hours	1300 MPa	189000 psi	ISO 899

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	IEC 60093
Dielectric Constant	3.8 @Frequency 100 Hz	3.8 @Frequency 100 Hz	IEC 60250
	3.8 @Frequency 1.00e+6 Hz	3.8 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	40.0 kV/mm	1020 kV/in	IEC 60243-1
Dissipation Factor	0.0010 @Frequency 100 Hz	0.0010 @Frequency 100 Hz	IEC 60250
	0.0050 @Frequency 1.00e+6 Hz	0.0050 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test Solution B; IEC 60112
	600 V	600 V	Test Solution A; IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	11.0 µm/m-°C @Temperature 23.0 - 55.0 °C	6.11 µin/in-°F @Temperature 73.4 - 131 °F	DIN 53752
Melting Point	167 °C	333 °F	DIN 53765
Maximum Service Temperature, Air	100 °C	212 °F
Deflection Temperature at 1.8 MPa (264 psi)	100 °C	212 °F	ISO 75
Vicat Softening Point	150 °C	302 °F	(50 °C/h / 50N) - B/50; ISO 306

Processing Properties	Metric	English	Comments
Melt Temperature	190 - 230 °C	374 - 446 °F	Injection-molding
Mold Temperature	60.0 - 120 °C	140 - 248 °F

Descriptive Properties
Color	Natural
Commercial Status	Active America
FDA	21 CFR 177.2470
Impact Modified	No
Primary Processing Technique	Injection Molding

物性表：

POM 的简介

聚甲醛学名聚氧化聚甲醛（简称POM）又称赛钢、特钢。

它是以甲醛等为原料聚合所得。

POM-H（聚甲醛均聚物），POM-K（聚甲醛共聚物）是高密度、高结晶度的热塑性工程塑料。

具有良好的物理、机械和化学性能，尤其是有优异的耐摩擦性能。

POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。

POM 电学性能

POM的电绝缘性较好，几乎不受温度和湿度的影响；介电常数和介电损耗在很宽的温度、湿度和频率范围内变化很小；耐电弧性极好，并可在高温下保持。POM的介电强度与厚度有关，厚度0.127mm时为82.7kV/mm，厚度为1.88mm时为23.6kV/mm。

POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。

POM 环境性能:

POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。

POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。 　　

POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。

应用范围：

POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。