类别：聚合物；热塑性塑料；丙烯酸（有机玻璃）；丙烯酸树脂，紫外线固化
材料说明：优异的防紫外线和耐候性，ASTM分类PMMA 0233v1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | weight gain after 24 hr. immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 1.6 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.6 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 45 | 45 | ASTM D785 |
| Tensile Strength, Ultimate | 37.9 MPa | 5500 psi | ASTM D638 |
| Tensile Modulus | 1.86 GPa | 270 ksi | ASTM D638 |
| Flexural Strength | <= 71.0 MPa | <= 10300 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.216 W/m-K | 1.50 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.9 °C | 192 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 °C | 175 °F | annealed; ASTM D648 |
| Vicat Softening Point | 86.1 °C | 187 °F | 50°C/hr; 50N; ASTM D1525 |
| 97.8 °C | 208 °F | 50°C/hr; 10N; ASTM D1525 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 @Temperature 22.8 °C |
1.49 @Temperature 73.0 °F |
ND; ASTM D542 |
| Haze | <= 2.0 % @Thickness 3.17 mm |
<= 2.0 % @Thickness 0.125 in |
ASTM D1003 |
| Transmission, Visible | 90 % @Thickness 3.17 mm |
90 % @Thickness 0.125 in |
ASTM D1003 |
示图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1396427082
联系邮箱；1396427082@qq.com
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1396427082
联系邮箱；1396427082@qq.com