| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | ||
| Water Absorption at Saturation | 1.0 % | 1.0 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | 50mm/min; ISO 527-2/1A | ||
| Elongation at Break | 40 % | 40 % | 50mm/min; ISO 527-2/1A | ||
| Elongation at Yield | 9.0 % | 9.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 1.95 GPa | 283 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Modulus | 1.85 GPa | 268 ksi | ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| 20.0 J/cm² @Temperature 30.0 °C |
95.2 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA | ||
| 0.900 J/cm² @Temperature 30.0 °C |
4.28 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 1700 MPa | 247000 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 950 MPa | 138000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |||
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 166 °C | 331 °F | ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 130 °C | 266 °F | B50 (50°C/h 50N); ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | hopper | ||
| 60.0 - 80.0 °C | 140 - 176 °F | cavity | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 170 - 180 °C | 338 - 356 °F | |||
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 3 | 190 - 200 °C | 374 - 392 °F | |||
| Zone 4 | 190 - 200 °C | 374 - 392 °F | |||
| Die Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Melt Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | |||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |||
| Moisture Content | 0.15 % | 0.15 % | Necessary low maximum | ||
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Hold Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Back Pressure | <= 2.00 MPa | <= 290 psi | |||
| Screw Speed | 70 rpm @Diameter 55.0 mm |
70 rpm @Diameter 2.17 in |
|||
| 100 rpm @Diameter 40.0 mm |
100 rpm @Diameter 1.57 in |
||||
| 150 rpm @Diameter 25.0 mm |
150 rpm @Diameter 0.984 in |
||||
| Hot-Working Temperature | 190 - 200 °C | 374 - 392 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | slow-medium | ||||
| Melt volume rate (MVR), cm³/10min | 4 | ||||
| MVR test load, kg | 2.16 | ||||
| MVR test temperature, °C | 190 | ||||
| Processing conditions acc. ISO | 9988-2 | ||||