Physical Properties |
Metric | English | Comments |
|---|---|---|---|
| Density | 0.0600 - 1.69 g/cc | 0.00217 - 0.0611 lb/in³ | Average value: 1.37 g/cc Grade Count:807 |
| Filler Content | 5.00 - 50.0 % | 5.00 - 50.0 % | Average value: 22.8 % Grade Count:55 |
| Water Absorption | 0.0150 - 4.00 % | 0.0150 - 4.00 % | Average value: 0.284 % Grade Count:253 |
| Moisture Absorption at Equilibrium | 0.000 - 1.30 % | 0.000 - 1.30 % | Average value: 0.532 % Grade Count:390 |
| Water Absorption at Saturation | 0.100 - 2.90 % | 0.100 - 2.90 % | Average value: 1.05 % Grade Count:289 |
| Additive Loading | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 18.5 % Grade Count:24 |
| Linear Mold Shrinkage | 0.000 - 0.0230 cm/cm | 0.000 - 0.0230 in/in | Average value: 0.00449 cm/cm Grade Count:699 |
| Linear Mold Shrinkage, Transverse | 0.000800 - 0.0170 cm/cm | 0.000800 - 0.0170 in/in | Average value: 0.00534 cm/cm Grade Count:241 |
| Melt Flow | 1.40 - 113 g/10 min | 1.40 - 113 g/10 min | Average value: 16.1 g/10 min Grade Count:456 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85.0 - 118 | 85.0 - 118 | Average value: 111 Grade Count:94 |
| Hardness, Rockwell R | 100 - 127 | 100 - 127 | Average value: 120 Grade Count:41 |
| Hardness, H358/30 | 95.0 - 170 MPa | 13800 - 24700 psi | Average value: 145 MPa Grade Count:98 |
| Hardness, Shore D | 72.0 - 93.0 | 72.0 - 93.0 | Average value: 83.7 Grade Count:15 |
| Ball Indentation Hardness | 165 - 170 MPa | 23900 - 24700 psi | Average value: 168 MPa Grade Count:4 |
| Tensile Strength, Ultimate | 1.70 - 281 MPa | 247 - 40800 psi | Average value: 122 MPa Grade Count:701 |
| Tensile Strength, Yield | 20.0 - 255 MPa | 2900 - 37000 psi | Average value: 113 MPa Grade Count:444 |
| Elongation at Break | 0.500 - 400 % | 0.500 - 400 % | Average value: 25.9 % Grade Count:771 |
| Elongation at Yield | 0.700 - 105 % | 0.700 - 105 % | Average value: 6.02 % Grade Count:344 |
| Modulus of Elasticity | 0.0370 - 42.0 GPa | 5.37 - 6090 ksi | Average value: 7.22 GPa Grade Count:739 |
| Flexural Yield Strength | 18.0 - 429 MPa | 2610 - 62200 psi | Average value: 184 MPa Grade Count:793 |
| Flexural Modulus | 0.380 - 32.6 GPa | 55.1 - 4730 ksi | Average value: 6.75 GPa Grade Count:792 |
| Compressive Yield Strength | 0.700 - 282 MPa | 102 - 40900 psi | Average value: 145 MPa Grade Count:48 |
| Compressive Modulus | 0.0460 - 6.47 GPa | 6.67 - 938 ksi | Average value: 3.28 GPa Grade Count:21 |
| Poissons Ratio | 0.300 - 0.440 | 0.300 - 0.440 | Average value: 0.380 Grade Count:20 |
| Shear Modulus | 0.0140 - 4.73 GPa | 2.03 - 685 ksi | Average value: 2.16 GPa Grade Count:10 |
| Shear Strength | 0.800 - 128 MPa | 116 - 18600 psi | Average value: 78.5 MPa Grade Count:18 |
| Izod Impact, Notched | 0.160 - 33.0 J/cm | 0.300 - 61.8 ft-lb/in | Average value: 3.40 J/cm Grade Count:672 |
| 0.300 - 1.20 J/cm @Temperature -30.0 - -30.0 °C |
0.562 - 2.25 ft-lb/in @Temperature -22.0 - -22.0 °F |
Average value: 0.567 J/cm Grade Count:122 | |
| Izod Impact, Unnotched | 0.110 J/cm - NB | 0.206 ft-lb/in - NB | Average value: 8.13 J/cm Grade Count:482 |
| 99.99 J/cm - NB @Temperature -30.0 - -30.0 °C |
187.3 ft-lb/in - NB @Temperature -22.0 - -22.0 °F |
Grade Count:13 | |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² - NB | 0.952 ft-lb/in² - NB | Average value: 7.56 kJ/m² Grade Count:342 |
| 2.00 kJ/m² - NB @Temperature -30.0 - -30.0 °C |
0.952 ft-lb/in² - NB @Temperature -22.0 - -22.0 °F |
Average value: 7.04 kJ/m² Grade Count:238 | |
| Izod Impact, Unnotched (ISO) | 0.700 kJ/m² - NB | 0.333 ft-lb/in² - NB | Average value: 43.4 kJ/m² Grade Count:274 |
| 13.0 kJ/m² - NB @Temperature -30.0 - -30.0 °C |
6.19 ft-lb/in² - NB @Temperature -22.0 - -22.0 °F |
Average value: 50.3 kJ/m² Grade Count:175 | |
| Charpy Impact Unnotched | 1.40 J/cm² - NB | 6.66 ft-lb/in² - NB | Average value: 4.92 J/cm² Grade Count:143 |
| 1.40 - 999.9 J/cm² @Temperature -30.0 - -30.0 °C |
6.66 - 4759 ft-lb/in² @Temperature -22.0 - -22.0 °F |
Average value: 4.32 J/cm² Grade Count:113 | |
| Charpy Impact, Notched | 0.200 - 1000 J/cm² | 0.952 - 4760 ft-lb/in² | Average value: 0.766 J/cm² Grade Count:239 |
| 0.300 - 1.50 J/cm² @Temperature -30.0 - -30.0 °C |
1.43 - 7.14 ft-lb/in² @Temperature -22.0 - -22.0 °F |
Average value: 0.614 J/cm² Grade Count:84 | |
| Gardner Impact | 2.26 - 36.0 J | 1.67 - 26.6 ft-lb | Average value: 29.1 J Grade Count:52 |
| Dart Drop, Total Energy | 2.00 - 380 J | 1.48 - 280 ft-lb | Average value: 29.0 J Grade Count:158 |
| 8.00 - 99.0 J @Temperature -30.0 - 0.000 °C |
5.90 - 73.0 ft-lb @Temperature -22.0 - 32.0 °F |
Average value: 76.7 J Grade Count:15 | |
| Falling Dart Impact | 4.90 - 21.4 J | 3.61 - 15.8 ft-lb | Average value: 9.18 J Grade Count:17 |
| Coefficient of Friction | 0.110 - 0.550 | 0.110 - 0.550 | Average value: 0.383 Grade Count:53 |
| Coefficient of Friction, Static | 0.110 - 0.600 | 0.110 - 0.600 | Average value: 0.384 Grade Count:41 |
| Tear Strength | 37.0 - 147 kN/m | 211 - 839 pli | Average value: 73.7 kN/m Grade Count:3 |
| K (wear) Factor | 24.2 - 5840 x 10-8 mm³/N-M | 12.0 - 2900 x 10-10 in³-min/ft-lb-hr | Average value: 508 x 10-8 mm³/N-M Grade Count:47 |
| Limiting Pressure Velocity | 0.0657 - 2.80 MPa-m/sec | 1880 - 79900 psi-ft/min | Average value: 1.40 MPa-m/sec Grade Count:10 |
| Taber Abrasion, mg/1000 Cycles | 2.00 - 60.0 | 2.00 - 60.0 | Average value: 16.0 Grade Count:97 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.100 - 6.70e+17 ohm-cm | 0.100 - 6.70e+17 ohm-cm | Average value: 2.85e+16 ohm-cm Grade Count:351 |
| Surface Resistance | 1.00 - 1.60e+17 ohm | 1.00 - 1.60e+17 ohm | Average value: 5.70e+15 ohm Grade Count:271 |
| Insulation Resistance | 1000 - 1.00e+12 ohm | 1000 - 1.00e+12 ohm | Average value: 7.08e+11 ohm Grade Count:24 |
| Static Decay | 0.0100 - 2.00 sec | 0.0100 - 2.00 sec | Average value: 1.04 sec Grade Count:48 |
| Shielding Effectiveness | 50.0 - 97.0 dB | 50.0 - 97.0 dB | Average value: 76.0 dB Grade Count:4 |
| Dielectric Constant | 2.70 - 6.80 | 2.70 - 6.80 | Average value: 3.28 Grade Count:221 |
| Dielectric Strength | 1.38 - 244 kV/mm | 35.0 - 6200 kV/in | Average value: 25.5 kV/mm Grade Count:249 |
| Dissipation Factor | 0.000500 - 0.266 | 0.000500 - 0.266 | Average value: 0.00487 Grade Count:247 |
| Arc Resistance | 0.000 - 180 sec | 0.000 - 180 sec | Average value: 126 sec Grade Count:130 |
| Comparative Tracking Index | 0.000 - 250 V | 0.000 - 250 V | Average value: 138 V Grade Count:262 |
| Hot Wire Ignition, HWI | 7.00 - 120 sec | 7.00 - 120 sec | Average value: 86.3 sec Grade Count:145 |
| High Amp Arc Ignition, HAI | 0.000 - 120 arcs | 0.000 - 120 arcs | Average value: 25.6 arcs Grade Count:145 |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 150 mm/min | 0.000 - 5.91 in/min | Average value: 82.0 mm/min Grade Count:130 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 2.70 - 120 µm/m-°C | 1.50 - 66.7 µin/in-°F | Average value: 38.6 µm/m-°C Grade Count:496 |
| CTE, linear, Transverse to Flow | 5.00 - 130 µm/m-°C | 2.78 - 72.2 µin/in-°F | Average value: 49.3 µm/m-°C Grade Count:392 |
| Thermal Conductivity | 0.0360 - 11.0 W/m-K | 0.250 - 76.3 BTU-in/hr-ft²-°F | Average value: 0.314 W/m-K Grade Count:222 |
| Melting Point | 215 - 238 °C | 419 - 460 °F | Average value: 227 °C Grade Count:3 |
| Maximum Service Temperature, Air | 170 - 300 °C | 338 - 572 °F | Average value: 176 °C Grade Count:43 |
| Transformation Temperature, Tg | 168 - 200 °C | 334 - 392 °F | Average value: 192 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 - 237 °C | 291 - 459 °F | Average value: 206 °C Grade Count:398 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.2 - 232 °C | 117 - 450 °F | Average value: 199 °C Grade Count:742 |
| Vicat Softening Point | 75.0 - 242 °C | 167 - 468 °F | Average value: 213 °C Grade Count:355 |
| Glass Transition Temp, Tg | 186 - 247 °C | 367 - 477 °F | Average value: 219 °C Grade Count:352 |
| UL RTI, Electrical | 105 - 180 °C | 221 - 356 °F | Average value: 152 °C Grade Count:169 |
| UL RTI, Mechanical with Impact | 105 - 180 °C | 221 - 356 °F | Average value: 151 °C Grade Count:168 |
| UL RTI, Mechanical without Impact | 105 - 180 °C | 221 - 356 °F | Average value: 152 °C Grade Count:168 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:396 |
| NBS Smoke Density | 0.700 - 6.00 | 0.700 - 6.00 | Average value: 1.59 Grade Count:19 |
| Oxygen Index | 39.7 - 54.0 % | 39.7 - 54.0 % | Average value: 47.0 % Grade Count:183 |
| Glow Wire Test | 850 - 960 °C | 1560 - 1760 °F | Average value: 936 °C Grade Count:76 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.00 % | 2.00 % | Average value: 2.00 % Grade Count:16 |
| Transmission, Visible | 58.0 - 90.0 % | 58.0 - 90.0 % | Average value: 85.7 % Grade Count:119 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 340 - 382 °C | 644 - 720 °F | Average value: 371 °C Grade Count:73 |
| Nozzle Temperature | 343 - 421 °C | 649 - 790 °F | Average value: 381 °C Grade Count:35 |
| Melt Temperature | 232 - 427 °C | 450 - 801 °F | Average value: 372 °C Grade Count:147 |
| Mold Temperature | 37.8 - 180 °C | 100 - 356 °F | Average value: 152 °C Grade Count:181 |
| Drying Temperature | 82.2 - 150 °C | 180 - 302 °F | Average value: 142 °C Grade Count:139 |
| Moisture Content | 0.0200 - 0.0400 % | 0.0200 - 0.0400 % | Average value: 0.0342 % Grade Count:96 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:68 |
| Injection Pressure | 82.7 - 124 MPa | 12000 - 18000 psi | Average value: 103 MPa Grade Count:110 |
| Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in |
|