| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 - 1.69 g/cc | 0.0470 - 0.0611 lb/in³ | Average value: 1.37 g/cc Grade Count:17 |
| Filler Content | 5.00 - 10.0 % | 5.00 - 10.0 % | Average value: 9.44 % Grade Count:9 |
| Water Absorption | 0.210 - 0.300 % | 0.210 - 0.300 % | Average value: 0.244 % Grade Count:13 |
| Linear Mold Shrinkage | 0.000500 - 0.00700 cm/cm | 0.000500 - 0.00700 in/in | Average value: 0.00475 cm/cm Grade Count:15 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 114 - 121 | 114 - 121 | Average value: 119 Grade Count:3 |
| Tensile Strength, Ultimate | 68.9 - 138 MPa | 10000 - 20000 psi | Average value: 115 MPa Grade Count:14 |
| Tensile Strength, Yield | 110 - 121 MPa | 16000 - 17500 psi | Average value: 115 MPa Grade Count:5 |
| Elongation at Break | 1.00 - 11.0 % | 1.00 - 11.0 % | Average value: 4.68 % Grade Count:13 |
| Elongation at Yield | 1.30 - 5.00 % | 1.30 - 5.00 % | Average value: 3.20 % Grade Count:3 |
| Modulus of Elasticity | 4.48 - 11.0 GPa | 650 - 1600 ksi | Average value: 6.01 GPa Grade Count:13 |
| Flexural Yield Strength | 124 - 214 MPa | 18000 - 31000 psi | Average value: 180 MPa Grade Count:16 |
| Flexural Modulus | 2.60 - 9.00 GPa | 377 - 1310 ksi | Average value: 4.99 GPa Grade Count:17 |
| Compressive Yield Strength | 152 MPa | 22000 psi | Average value: 152 MPa Grade Count:3 |
| Izod Impact, Notched | 0.320 - 0.587 J/cm | 0.600 - 1.10 ft-lb/in | Average value: 0.516 J/cm Grade Count:15 |
| Izod Impact, Unnotched | 2.14 - 12.8 J/cm | 4.00 - 24.0 ft-lb/in | Average value: 6.01 J/cm Grade Count:11 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+17 ohm-cm | 1000 - 1.00e+17 ohm-cm | Average value: 2.40e+16 ohm-cm Grade Count:10 |
| Surface Resistance | 10000 - 1.00e+12 ohm | 10000 - 1.00e+12 ohm | Average value: 3.50e+11 ohm Grade Count:3 |
| Dielectric Constant | 3.50 - 3.60 | 3.50 - 3.60 | Average value: 3.55 Grade Count:4 |
| Dielectric Strength | 19.7 - 27.6 kV/mm | 500 - 700 kV/in | Average value: 22.2 kV/mm Grade Count:6 |
| Dissipation Factor | 0.00140 - 0.00500 | 0.00140 - 0.00500 | Average value: 0.00348 Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.0 - 54.0 µm/m-°C | 7.78 - 30.0 µin/in-°F | Average value: 35.3 µm/m-°C Grade Count:8 |
| Thermal Conductivity | 0.176 - 0.500 W/m-K | 1.22 - 3.47 BTU-in/hr-ft²-°F | Average value: 0.271 W/m-K Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 196 - 223 °C | 385 - 433 °F | Average value: 210 °C Grade Count:11 |
| Deflection Temperature at 1.8 MPa (264 psi) | 189 - 221 °C | 372 - 430 °F | Average value: 206 °C Grade Count:15 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:8 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 349 - 382 °C | 660 - 720 °F | Average value: 371 °C Grade Count:8 |
| Nozzle Temperature | 343 - 400 °C | 649 - 752 °F | Average value: 374 °C Grade Count:3 |
| Melt Temperature | 330 - 400 °C | 626 - 752 °F | Average value: 367 °C Grade Count:7 |
| Mold Temperature | 107 - 180 °C | 225 - 356 °F | Average value: 156 °C Grade Count:12 |
| Drying Temperature | 120 - 150 °C | 248 - 302 °F | Average value: 142 °C Grade Count:7 |
| Moisture Content | 0.0200 - 0.0400 % | 0.0200 - 0.0400 % | Average value: 0.0350 % Grade Count:4 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:3 |
| Injection Pressure | 82.7 - 124 MPa | 12000 - 18000 ps | |