| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 1183 |
| Melt Flow | 17.04 g/10 min @Load 2.16 kg, Temperature 190 °C |
17.04 g/10 min @Load 4.76 lb, Temperature 374 °F |
Calculated from Volume flow Rate: 12 cm3/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Elongation at Break | 30 % | 30 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Elongation at Yield | 11 % | 11 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Tensile Modulus | 2.90 GPa | 421 ksi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 1 mm/min |
| Charpy Impact Unnotched | 15.0 J/cm² @Thickness 4.00 mm, Temperature 23.0 °C |
71.4 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA |
| 0.800 J/cm² @Thickness 4.00 mm, Temperature 23.0 °C |
3.81 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA |
|