类别：聚合物；热塑性塑料；丙烯酸（有机玻璃）；丙烯酸
材料说明：有机玻璃压克力铸®GS 249是另一个专门开发的满足更高的要求的航空业，但另外交联。与未交联的丙烯酸树脂相比，它具有更高的耐介质性，引起应力开裂和提高热变形阻力。有机玻璃®GS 249也特别适合于拉伸，从而进一步提高其性能在正常状态。典型应用在民用飞机客舱窗户，加压机舱，驾驶舱的玻璃窗，檐篷和挡风玻璃。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183, ASTM D792 | ||
| Water Absorption | 0.20 % | 0.20 % | MIL-P-8184 | ||
| Water Absorption at Saturation | 2.1 % | 2.1 % | MIL-P-8184 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-2/1B/5, ASTM D638 | ||
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-2/1B/5, ASTM D 638 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
EN 2155-12, ASTM D696 | ||
| Maximum Service Temperature, Air | 113 °C | 235 °F | ISO 71-2Ae, ASTM D648 | ||
| Vicat Softening Point | 118 °C | 244 °F | ISO 306-B-50 | ||
| Flame Spread | 15.2 mm/min | 0.600 in/min | Fire Rating; ASTM D635 | ||
| 20.0 mm/min | 0.787 in/min | Fire Rating; EN 3844-2 | |||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.49 | 1.49 | ISO 489, ASTM D542 | ||
| Haze | 1.5 % | 1.5 % | Original State; EN 2155-9, ASTM D1003 | ||
| 2.2 % | 2.2 % | after artificial weathering; EN 2155-9, ASTM D1003 | |||
| Transmission, Visible | 89 % | 89 % | after artificial weathering; ASTM D1003 | ||
| 91 % | 91 % | Original State; EN 2155-5, ASTM D1003 | |||
| UV Transmittance | <= 1.0 % @Wavelength 290 - 330 nm |
<= 1.0 % @Wavelength 290 - 330 nm |
|||
| De |
|||||
| Angular Deviation | Max 4 minutes | EN 2155-7 (ASTM D637) |
|||
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com