| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.22 % | 0.22 % | 24 hours at 73°C |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
|
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 59.3 MPa @Thickness 3.17 mm |
8600 psi @Thickness 0.125 in |
|
| Elongation at Break | 50 % @Thickness 3.17 mm |
50 % @Thickness 0.125 in |
|
| Flexural Yield Strength | 85.5 MPa @Thickness 3.17 mm |
12400 psi @Thickness 0.125 in |
|
| Flexural Modulus | 2.55 GPa @Thickness 3.17 mm |
370 ksi @Thickness 0.125 in |
|
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.17 mm |
0.993 ft-lb/in @Thickness 0.125 in |
|
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 °C | 329 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 165 - 180 °C | 329 - 356 °F | |
| Middle Barrel Temperature | 175 - 195 °C | 347 - 383 °F | |
| Front Barrel Temperature | 180 - 195 °C | 356 - 383 °F | |
| Nozzle Temperature | 180 - 195 °C | 356 - 383 °F | |
| Melt Temperature | 185 - 220 °C | 365 - 428 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Injection Pressure | 48.3 - 117 MPa | 7000 - 17000 psi | |
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM F20-52 图：