类别：聚合物；热塑性塑料；丙烯酸（有机玻璃）；丙烯酸，冲击改性
材料说明：该聚二-甲基丙烯酸甲脂®影响PMMA系列提供冲击的最佳组合，化学和耐热性以及提供刚性和表面硬度。在聚二-甲基丙烯酸甲脂®系列的等级可以通过注塑或挤出加工。
物性表：| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Water Absorption | 0.36 % | 0.36 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | |
| Melt Flow | 3.7 g/10 min | 3.7 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 30 | 30 | ISO 2039-2 |
| Tensile Strength | 38.0 MPa | 5510 psi | ISO 527 |
| Elongation at Break | 33 % | 33 % | ISO 527 |
| Flexural Strength | 54.0 MPa | 7830 psi | ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.90 kJ/m² | 3.28 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.780 J/cm² | 3.71 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 µm/m-°C | 66.7 µin/in-°F | ASTM E831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ISO 75A |
| Vicat Softening Point | 82.0 °C | 180 °F | ISO 306B |
| 94.0 °C | 201 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 3.0 % | 3.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |