| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.330 % | 0.330 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.022 cm/cm @Time 86400 sec |
0.022 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0221 cm/cm @Time 86400 sec |
0.0221 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0214 cm/cm @Time 86400 sec |
0.0214 in/in @Time 24.0 hour |
ISO 294 |
| 0.023 cm/cm @Time 86400 sec |
0.023 in/in @Time 24.0 hour |
ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
| 59.0 MPa | 8560 psi | ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM D638 |
| 60.0 MPa | 8700 psi | ISO 527 | |
| Elongation at Break | 13.3 % | 13.3 % | ISO 527 |
| 32.4 % | 32.4 % | ASTM D638 | |
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527 |
| 9.3 % | 9.3 % | ASTM D638 | |
| Tensile Modulus | 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 |
| 2.56 GPa | 371 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO 178 |
| 84.0 MPa | 12200 psi | ASTM D790 | |
| Flexural Modulus | 2.42 GPa | 351 ksi | ASTM D790 |
| 2.42 GPa | 351 ksi | ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.56 J/cm | 25.40 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.38 | 0.38 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.24 | 0.24 | ASTM D3702 Modified |
| K (wear) Factor | 20.1 x 10-8 mm³/N-M | 10.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 115 µm/m-°C @Temperature -40.0 - 40.0 °C |
63.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 115 µm/m-°C @Temperature -40.0 - 40.0 °C |
63.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 111 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 111 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM K2000XXH 图：