| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| 1.473 g/cc | 0.05322 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.210 % | 0.210 % | 50% RH, 24 hrs; ASTM D570 |
| 0.320 % | 0.320 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 |
| 77.0 MPa | 11200 psi | ASTM D638 | |
| Elongation at Break | 1.0 % | 1.0 % | ISO 527 |
| 1.1 % | 1.1 % | ASTM D638 | |
| Tensile Modulus | 10.17 GPa | 1475 ksi | 1 mm/min; ISO 527 |
| 10.2 GPa | 1480 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| 114 MPa | 16500 psi | ASTM D790 | |
| Flexural Modulus | 7.14 GPa | 1040 ksi | ASTM D790 |
| 8.27 GPa | 1200 ksi | ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.28 J/cm | 2.40 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.31 | 0.31 | ASTM D3702 Modified |
| K (wear) Factor | 407 x 10-8 mm³/N-M | 202 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 10 - 10000 ohm-cm | 10 - 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 10 - 10000 ohm | 10 - 10000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 66.0 °C @Thickness 3.20 mm |
151 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM KEP33 图：