| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| 1.443 g/cc | 0.05213 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.015 - 0.035 cm/cm @Time 86400 sec |
0.015 - 0.035 in/in @Time 24.0 hour |
ASTM D955 |
| 0.015 - 0.035 cm/cm @Time 86400 sec |
0.015 - 0.035 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.015 - 0.035 cm/cm @Time 86400 sec |
0.015 - 0.035 in/in @Time 24.0 hour |
ASTM D955 |
| 0.015 - 0.035 cm/cm @Time 86400 sec |
0.015 - 0.035 in/in @Time 24.0 hour |
ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527 |
| 47.0 MPa | 6820 psi | ASTM D638 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | ASTM D638 |
| 53.0 MPa | 7690 psi | ISO 527 | |
| Elongation at Break | 10.2 % | 10.2 % | ASTM D638 |
| 18.1 % | 18.1 % | ISO 527 | |
| Elongation at Yield | 3.8 % | 3.8 % | ASTM D638 |
| 4.0 % | 4.0 % | ISO 527 | |
| Tensile Modulus | 3.46 GPa | 502 ksi | 1 mm/min; ISO 527 |
| 3.48 GPa | 505 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 96.0 MPa | 13900 psi | ISO 178 |
| 100 MPa | 14500 psi | ASTM D790 | |
| Flexural Modulus | 3.01 GPa | 437 ksi | ASTM D790 |
| 3.01 GPa | 437 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.73 J/cm | 6.99 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J | 2.21 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 100 - 1.00e+6 ohm-cm | 100 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM KX02764 图：