杜邦高性能聚合物聚甲醛（POM）®100AF缩醛
类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋
材料说明：20%®纤维填充聚四氟乙烯的高粘度缩醛均聚物具有低磨损和低摩擦
Delrin 100AF是一种高粘度缩醛均聚物含有20%的聚四氟乙烯纤维。它是专为需要低磨损和/或低摩擦的程序应用
物性表：
物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 | ||
| Viscosity | 111000 cP @Shear Rate 5000 1/s, Temperature 230 °C |
111000 cP @Shear Rate 5000 1/s, Temperature 446 °F |
ISO 11403-1 -2 | ||
| 128000 cP @Shear Rate 5000 1/s, Temperature 215 °C |
128000 cP @Shear Rate 5000 1/s, Temperature 419 °F |
ISO 11403-1 -2 | |||
| 151000 cP @Shear Rate 5000 1/s, Temperature 200 °C |
151000 cP @Shear Rate 5000 1/s, Temperature 392 °F |
ISO 11403-1 -2 | |||
| 441000 cP @Shear Rate 500 1/s, Temperature 230 °C |
441000 cP @Shear Rate 500 1/s, Temperature 446 °F |
ISO 11403-1 -2 | |||
| 509000 cP @Shear Rate 500 1/s, Temperature 215 °C |
509000 cP @Shear Rate 500 1/s, Temperature 419 °F |
ISO 11403-1 -2 | |||
| 598000 cP @Shear Rate 500 1/s, Temperature 200 °C |
598000 cP @Shear Rate 500 1/s, Temperature 392 °F |
ISO 11403-1 -2 | |||
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ISO 294-4 2577 | ||
| Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527-1/-2 | ||
| Elongation at Break | 15 % | 15 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| De |
|||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Part Marking Code | >POM-SF20< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Sheet Extrusion | |||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | POM-SF20 | ISO 1043 | |||
| UL recognition | UL | ||||