  4. 杜邦高性能聚合物聚甲醛POM 100al NC010乙缩醛

杜邦高性能聚合物聚甲醛POM 100al NC010乙缩醛

POM 100al NC010 材料说明：低磨损和低摩擦润滑高粘度缩醛均聚物 聚甲醛100al NC010未增强的高粘度润滑缩醛均聚物树脂含有低摩擦磨损与润滑系统和一个先进的金属
 杜邦高性能聚合物聚甲醛（POM）®100al NC010乙缩醛
类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋
材料说明：低磨损和低摩擦润滑高粘度缩醛均聚物
聚甲醛100al NC010未增强的高粘度润滑缩醛均聚物树脂含有低摩擦磨损与润滑系统和一个先进的金属
物性表：

 
Physical Properties Metric English Comments
Density  1.40 g/cc 0.0506 lb/in³ ISO 1183
Viscosity   111000 cP
@Shear Rate 5000 1/s,
Temperature 230 °C		 111000 cP
@Shear Rate 5000 1/s,
Temperature 446 °F		 ISO 11403-1 -2
  129000 cP
@Shear Rate 5000 1/s,
Temperature 215 °C		 129000 cP
@Shear Rate 5000 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  152000 cP
@Shear Rate 5000 1/s,
Temperature 200 °C		 152000 cP
@Shear Rate 5000 1/s,
Temperature 392 °F		 ISO 11403-1 -2
  432000 cP
@Shear Rate 500 1/s,
Temperature 230 °C		 432000 cP
@Shear Rate 500 1/s,
Temperature 446 °F		 ISO 11403-1 -2
  502000 cP
@Shear Rate 500 1/s,
Temperature 215 °C		 502000 cP
@Shear Rate 500 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  593000 cP
@Shear Rate 500 1/s,
Temperature 200 °C		 593000 cP
@Shear Rate 500 1/s,
Temperature 392 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.020 cm/cm 0.020 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.018 cm/cm 0.018 in/in ISO 294-4 2577
Melt Flow  2.5 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 2.5 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   44.9 MPa
@Strain 2.20 %,
Temperature 23.0 °C		 6510 psi
@Strain 2.20 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  57.6 MPa
@Strain 1.80 %,
Temperature -40.0 °C		 8350 psi
@Strain 1.80 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  64.5 MPa
@Strain 8.00 %,
Temperature 23.0 °C		 9350 psi
@Strain 8.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  65.6 MPa
@Strain 15.0 %,
Temperature 23.0 °C		 9510 psi
@Strain 15.0 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  94.1 MPa
@Strain 7.00 %,
Temperature -40.0 °C		 13600 psi
@Strain 7.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  96.0 MPa
@Strain 13.0 %,
Temperature -40.0 °C		 13900 psi
@Strain 13.0 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  70.0 MPa 10200 psi ISO 527-1/-2
Elongation at Break  45 % 45 % Nominal; ISO 527-1/-2
Elongation at Yield  18 % 18 % ISO 527-1/-2
Tensile Modulus  3.00 GPa 435 ksi ISO 527-1/-2
Flexural Modulus  2.80 GPa 406 ksi ISO 178
Secant Modulus   0.141 GPa
@Strain 19.0 %,
Temperature 100 °C		 20.4 ksi
@Strain 19.0 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.192 GPa
@Strain 19.0 %,
Temperature 80.0 °C		 27.8 ksi
@Strain 19.0 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.286 GPa
@Strain 9.00 %,
Temperature 100 °C		 41.4 ksi
@Strain 9.00 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.386 GPa
@Strain 17.0 %,
Temperature 23.0 °C		 56.1 ksi
@Strain 17.0 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.393 GPa
@Strain 9.00 %,
Temperature 80.0 °C		 57.0 ksi
@Strain 9.00 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.640 GPa
@Strain 15.0 %,
Temperature -40.0 °C		 92.8 ksi
@Strain 15.0 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  0.80625 GPa
@Strain 8.00 %,
Temperature 23.0 °C		 116.94 ksi
@Strain 8.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.854 GPa
@Strain 2.40 %,
Temperature 100 °C		 124 ksi
@Strain 2.40 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.14 GPa
@Strain 2.40 %,
Temperature 80.0 °C		 166 ksi
@Strain 2.40 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.34 GPa
@Strain 7.00 %,
Temperature -40.0 °C		 195 ksi
@Strain 7.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.04 GPa
@Strain 2.20 %,
Temperature 23.0 °C		 296 ksi
@Strain 2.20 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  3.20 GPa
@Strain 1.80 %,
Temperature -40.0 °C		 464 ksi
@Strain 1.80 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  8.00 kJ/m² 3.81 ft-lb/in² ISO 180/1A
Charpy Impact Unnotched  25.0 J/cm² 119 ft-lb/in² ISO 179/1eU
  17.0 J/cm²
@Temperature -30.0 °C		 80.9 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.900 J/cm² 4.28 ft-lb/in² ISO 179/1eA
  0.700 J/cm²
@Temperature -30.0 °C		 3.33 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  163 °C 325 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  97.0 °C 207 °F ISO 75-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Emissions <8 mg/kg VDA 275
Part Marking Code >POM-S< ISO 11469
Processing Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
  Sheet Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM-S ISO 1043
UL recognition UL  
  UL
图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-38458.html

免责声明: 本文 杜邦高性能聚合物聚甲醛POM 100al NC010乙缩醛 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4