类别:聚合物;热塑性;聚甲醛(POM);缩醛均聚物,无筋
材料说明:核中高粘度缩醛均聚物
Delrin 311DP是中高粘度缩醛均聚物具有增强的结晶和部分性能和易于加工的平衡。它具有改善高强度和高强度
物性表:Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | ||
Water Absorption | 0.90 % @Thickness 2.00 mm |
0.90 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
Moisture Absorption | 0.200 % @Thickness 2.00 mm |
0.200 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | ISO 294-4 2577 | ||
Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 2577 | ||
Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
cm³/10min; ISO 1133 | ||
7.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | |||
Mechanical Properties | Metric | English | Comments | ||
Tensile Stress | 4.47 MPa @Strain 0.150 %, Temperature 40.0 °C |
648 psi @Strain 0.150 %, Temperature 104 °F |
ISO 11403-1 -2 | ||
6.31 MPa @Strain 0.460 %, Temperature 90.0 °C |
915 psi @Strain 0.460 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
9.92 MPa @Strain 0.290 %, Temperature 23.0 °C |
1440 psi @Strain 0.290 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
21.3 MPa @Strain 0.611 %, Temperature 0.000 °C |
3090 psi @Strain 0.611 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
24.56 MPa @Strain 2.58 %, Temperature 90.0 °C |
3562 psi @Strain 2.58 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
27.19 MPa @Strain 0.730 %, Temperature -20.0 °C |
3944 psi @Strain 0.730 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
27.45 MPa @Strain 0.690 %, Temperature -40.0 °C |
3981 psi @Strain 0.690 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
32.21 MPa @Strain 4.88 %, Temperature 90.0 °C |
4672 psi @Strain 4.88 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
37.04 MPa @Strain 1.71 %, Temperature 40.0 °C |
5372 psi @Strain 1.71 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
50.17 MPa @Strain 2.29 %, Temperature 23.0 °C |
7277 psi @Strain 2.29 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
54.39 MPa @Strain 3.93 %, Temperature 40.0 °C |
7889 psi @Strain 3.93 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
56.48 MPa @Strain 2.29 %, Temperature 0.000 °C |
8192 psi @Strain 2.29 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
60.28 MPa @Strain 6.41 %, Temperature 40.0 °C |
8743 psi @Strain 6.41 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
64.31 MPa @Strain 4.58 %, Temperature 23.0 °C |
9327 psi @Strain 4.58 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
68.72 MPa @Strain 7.21 %, Temperature 23.0 °C |
9967 psi @Strain 7.21 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
72.85 MPa @Strain 4.53 %, Temperature 0.000 °C |
10570 psi @Strain 4.53 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
75.19 MPa @Strain 3.25 %, Temperature -20.0 °C |
10910 psi @Strain 3.25 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
77.78 MPa @Strain 7.12 %, Temperature 0.000 °C |
11280 psi @Strain 7.12 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
80.68 MPa @Strain 3.12 %, Temperature -40.0 °C |
11700 psi @Strain 3.12 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
85.65 MPa @Strain 5.67 %, Temperature -20.0 °C |
12420 psi @Strain 5.67 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
88.5 MPa @Strain 8.47 %, Temperature -20.0 °C |
12800 psi @Strain 8.47 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
93.8 MPa @Strain 5.11 %, Temperature -40.0 °C |
13600 psi @Strain 5.11 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
97.6 MPa @Strain 7.38 %, Temperature -40.0 °C |
14200 psi @Strain 7.38 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | ISO 527-1/-2 | ||
Elongation at Break | 35 % | 35 % | Nominal; ISO 527-1/-2 | ||
Elongation at Yield | 15 % | 15 % | ISO 527-1/-2 | ||
Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527-1/-2 | ||
Flexural Strength | 86.0 MPa @Strain 3.50 % |
12500 psi @Strain 3.50 % |
ISO 178 | ||
Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 | ||
Secant Modulus | 0.570 GPa @Strain 5.00 %, Temperature 100 °C |
82.7 ksi @Strain 5.00 %, Temperature 212 °F |
ISO 11403-1 -2 | ||
0.591 GPa @Strain 7.00 %, Temperature 80.0 °C |
85.8 ksi @Strain 7.00 %, Temperature 176 °F |
ISO 11403-1 -2 | |||
0.736 GPa @Strain 3.30 %, Temperature 100 °C |
107 ksi @Strain 3.30 %, Temperature 212 °F |
ISO 11403-1 -2 | |||
0.754 GPa @Strain 8.18 %, Temperature 40.0 °C |
109 ksi @Strain 8.18 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
0.9075 GPa @Strain 4.00 %, Temperature 80.0 °C |
131.6 ksi @Strain 4.00 %, Temperature 176 °F |
ISO 11403-1 -2 | |||
0.99375 GPa @Strain 1.60 %, Temperature 100 °C |
144.13 ksi @Strain 1.60 %, Temperature 212 °F |
ISO 11403-1 -2 | |||
1.15 GPa @Strain 0.400 %, Temperature 100 °C |
167 ksi @Strain 0.400 %, Temperature 212 °F |
ISO 11403-1 -2 | |||
1.2163 GPa @Strain 5.46 %, Temperature 23.0 °C |
176.41 ksi @Strain 5.46 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
1.22 GPa @Strain 4.70 %, Temperature 40.0 °C |
176 ksi @Strain 4.70 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
1.255 GPa @Strain 2.00 %, Temperature 80.0 °C |
182.0 ksi @Strain 2.00 %, Temperature 176 °F |
ISO 11403-1 -2 | |||
1.33 GPa @Strain 6.56 %, Temperature -20.0 °C |
192 ksi @Strain 6.56 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
1.40 GPa @Strain 5.38 %, Temperature 0.000 °C |
203 ksi @Strain 5.38 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
1.63 GPa @Strain 5.86 %, Temperature -40.0 °C |
237 ksi @Strain 5.86 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
1.64 GPa @Strain 0.500 %, Temperature 80.0 °C |
238 ksi @Strain 0.500 %, Temperature 176 °F |
ISO 11403-1 -2 | |||
2.17 GPa @Strain 1.71 %, Temperature 40.0 °C |
314 ksi @Strain 1.71 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
2.19 GPa @Strain 2.29 %, Temperature 23.0 °C |
318 ksi @Strain 2.29 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
2.31 GPa @Strain 3.25 %, Temperature -20.0 °C |
336 ksi @Strain 3.25 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
2.47 GPa @Strain 2.29 %, Temperature 0.000 °C |
358 ksi @Strain 2.29 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
2.5859 GPa @Strain 3.12 %, Temperature -40.0 °C |
375.06 ksi @Strain 3.12 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
2.98 GPa @Strain 0.150 %, Temperature 40.0 °C |
432 ksi @Strain 0.150 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
3.42 GPa @Strain 0.290 %, Temperature 23.0 °C |
496 ksi @Strain 0.290 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
3.49 GPa @Strain 0.611 %, Temperature 0.000 °C |
506 ksi @Strain 0.611 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
3.72 GPa @Strain 0.730 %, Temperature -20.0 °C |
540 ksi @Strain 0.730 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
3.98 GPa @Strain 0.690 %, Temperature -40.0 °C |
577 ksi @Strain 0.690 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180/1A | ||
8.00 kJ/m² @Temperature -40.0 °C |
3.81 ft-lb/in² @Temperature -40.0 °F |
ISO 180/1A | |||
Charpy Impact Unnotched | 30.0 J/cm² | 143 ft-lb/in² | ISO 179/1eU | ||
25.0 J/cm² @Temperature -30.0 °C |
119 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA | ||
0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
Dielectric Constant | 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | ||
3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
Thermal Properties | Metric | English | Comments | ||
CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | ISO 75-1/-2 | ||
Vicat Softening Point | 160 °C | 320 °F | 50°C/h 50N; ISO 306 | ||
Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 | |||
De |
|||||
Additives | Lubricants | ||||
Release agent | |||||
Delivery form | Pellets | ||||
Emissions | <8 mg/kg | VDA 275 | |||
Part Marking Code | >POM< | ISO 11469 | |||
Processing | Injection Moulding | ||||
Other Extrusion | |||||
Profile Extrusion | |||||
Sheet Extrusion | |||||
Regional Availability | Asia Pacific | ||||
Europe | |||||
Global | |||||
Near East/Africa | |||||
North America | |||||
South and Central America | |||||
Resin Identification | POM | ISO 1043 | |||
UL recognition | UL | ||||
UL |
上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
欢迎新老客户来电咨询;
联系人:李先生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com