杜邦高性能聚合物聚甲醛POM 500cl NC010

POM 500cl NC010 材料说明：润滑介质粘度缩醛均聚物具有低磨损和低摩擦 聚甲醛是一500cl介质粘度缩醛均聚物树脂含有化学润滑剂专为低磨损和摩擦对金属
 杜邦高性能聚合物聚甲醛（POM）500cl NC010乙缩醛
类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋
材料说明：润滑介质粘度缩醛均聚物具有低磨损和低摩擦
聚甲醛是一500cl介质粘度缩醛均聚物树脂含有化学润滑剂专为低磨损和摩擦对金属。
物性表：

 
Physical Properties Metric English Comments
Density  1.41 g/cc 0.0509 lb/in³ ISO 1183
Water Absorption  1.0 %
@Thickness 2.00 mm		 1.0 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.250 %
@Thickness 2.00 mm		 0.250 %
@Thickness 0.0787 in		 Sim. to ISO 62
Linear Mold Shrinkage, Flow  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.018 cm/cm 0.018 in/in ISO 294-4 2577
Melt Flow   12 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 12 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 cm³/10min; ISO 1133
  15 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 15 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  92 92 ISO 2039-2
Hardness, Rockwell R  120 120 ISO 2039-2
Tensile Stress   9.90 MPa
@Strain 1.10 %,
Temperature 90.0 °C		 1440 psi
@Strain 1.10 %,
Temperature 194 °F		 ISO 11403-1 -2
  25.6 MPa
@Strain 4.60 %,
Temperature 90.0 °C		 3710 psi
@Strain 4.60 %,
Temperature 194 °F		 ISO 11403-1 -2
  27.5 MPa
@Strain 1.40 %,
Temperature 40.0 °C		 3990 psi
@Strain 1.40 %,
Temperature 104 °F		 ISO 11403-1 -2
  28.9 MPa
@Strain 1.10 %,
Temperature 23.0 °C		 4190 psi
@Strain 1.10 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  31.4 MPa
@Strain 8.00 %,
Temperature 90.0 °C		 4550 psi
@Strain 8.00 %,
Temperature 194 °F		 ISO 11403-1 -2
  32.6 MPa
@Strain 11.4 %,
Temperature 90.0 °C		 4730 psi
@Strain 11.4 %,
Temperature 194 °F		 ISO 11403-1 -2
  41.8 MPa
@Strain 1.50 %,
Temperature 0.000 °C		 6060 psi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  45.7 MPa
@Strain 1.40 %,
Temperature -20.0 °C		 6630 psi
@Strain 1.40 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  52.3 MPa
@Strain 1.60 %,
Temperature -40.0 °C		 7590 psi
@Strain 1.60 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  52.9 MPa
@Strain 5.50 %,
Temperature 40.0 °C		 7670 psi
@Strain 5.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  57.1 MPa
@Strain 9.60 %,
Temperature 40.0 °C		 8280 psi
@Strain 9.60 %,
Temperature 104 °F		 ISO 11403-1 -2
  58.0 MPa
@Strain 4.40 %,
Temperature 23.0 °C		 8410 psi
@Strain 4.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  63.8 MPa
@Strain 7.60 %,
Temperature 23.0 °C		 9250 psi
@Strain 7.60 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  65.0 MPa
@Strain 10.9 %,
Temperature 23.0 °C		 9430 psi
@Strain 10.9 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  70.9 MPa
@Strain 5.80 %,
Temperature 0.000 °C		 10300 psi
@Strain 5.80 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  73.6 MPa
@Strain 10.2 %,
Temperature 0.000 °C		 10700 psi
@Strain 10.2 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  74.1 MPa
@Strain 14.6 %,
Temperature 0.000 °C		 10700 psi
@Strain 14.6 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  78.2 MPa
@Strain 5.50 %,
Temperature -20.0 °C		 11300 psi
@Strain 5.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  81.9 MPa
@Strain 9.70 %,
Temperature -20.0 °C		 11900 psi
@Strain 9.70 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  82.2 MPa
@Strain 13.8 %,
Temperature -20.0 °C		 11900 psi
@Strain 13.8 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  93.9 MPa
@Strain 6.40 %,
Temperature -40.0 °C		 13600 psi
@Strain 6.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  96.7 MPa
@Strain 11.1 %,
Temperature -40.0 °C		 14000 psi
@Strain 11.1 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  97.1 MPa
@Strain 15.9 %,
Temperature -40.0 °C		 14100 psi
@Strain 15.9 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  67.0 MPa 9720 psi ISO 527-1/-2
Elongation at Break  25 % 25 % Nominal; ISO 527-1/-2
Elongation at Yield  15 % 15 % ISO 527-1/-2
Tensile Modulus  3.10 GPa 450 ksi ISO 527-1/-2
Flexural Modulus  2.90 GPa 421 ksi ISO 178
Shear Modulus   0.222 GPa
@Temperature 120 °C		 32.2 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.509 GPa
@Temperature 70.0 °C		 73.8 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  0.907 GPa
@Temperature 20.0 °C		 132 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  1.105 GPa
@Temperature -20.0 °C		 160.3 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.29 GPa
@Temperature -50.0 °C		 187 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   0.308 GPa
@Strain 9.80 %,
Temperature 100 °C		 44.7 ksi
@Strain 9.80 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.450 GPa
@Strain 8.60 %,
Temperature 80.0 °C		 65.3 ksi
@Strain 8.60 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.498 GPa
@Strain 5.40 %,
Temperature 100 °C		 72.3 ksi
@Strain 5.40 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.522 GPa
@Strain 11.0 %,
Temperature 40.0 °C		 75.7 ksi
@Strain 11.0 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.632 GPa
@Strain 11.7 %,
Temperature 0.000 °C		 91.7 ksi
@Strain 11.7 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.737 GPa
@Strain 4.30 %,
Temperature 80.0 °C		 107 ksi
@Strain 4.30 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.74023 GPa
@Strain 8.70 %,
Temperature 23.0 °C		 107.36 ksi
@Strain 8.70 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.745 GPa
@Strain 11.0 %,
Temperature -20.0 °C		 108 ksi
@Strain 11.0 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  0.762 GPa
@Strain 12.7 %,
Temperature -40.0 °C		 111 ksi
@Strain 12.7 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  0.764 GPa
@Strain 2.20 %,
Temperature 100 °C		 111 ksi
@Strain 2.20 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.962 GPa
@Strain 5.50 %,
Temperature 40.0 °C		 140 ksi
@Strain 5.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.22 GPa
@Strain 5.80 %,
Temperature 0.000 °C		 177 ksi
@Strain 5.80 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.23 GPa
@Strain 1.10 %,
Temperature 80.0 °C		 178 ksi
@Strain 1.10 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.32 GPa
@Strain 4.40 %,
Temperature 23.0 °C		 191 ksi
@Strain 4.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.42 GPa
@Strain 5.50 %,
Temperature -20.0 °C		 206 ksi
@Strain 5.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  1.47 GPa
@Strain 6.40 %,
Temperature -40.0 °C		 213 ksi
@Strain 6.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.96 GPa
@Strain 1.40 %,
Temperature 40.0 °C		 285 ksi
@Strain 1.40 %,
Temperature 104 °F		 ISO 11403-1 -2
  2.63 GPa
@Strain 1.10 %,
Temperature 23.0 °C		 381 ksi
@Strain 1.10 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.79 GPa
@Strain 1.50 %,
Temperature 0.000 °C		 404 ksi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.26 GPa
@Strain 1.40 %,
Temperature -20.0 °C		 473 ksi
@Strain 1.40 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  3.27 GPa
@Strain 1.60 %,
Temperature -40.0 °C		 474 ksi
@Strain 1.60 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  9.00 kJ/m² 4.28 ft-lb/in² ISO 180/1A
  9.00 kJ/m²
@Temperature -40.0 °C		 4.28 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
Charpy Impact Unnotched  35.0 J/cm² 167 ft-lb/in² ISO 179/1eU
  29.0 J/cm²
@Temperature -30.0 °C		 138 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.800 J/cm² 3.81 ft-lb/in² ISO 179/1eA
  0.700 J/cm²
@Temperature -30.0 °C		 3.33 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
 
Electrical Properties Metric English Comments
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm IEC 60093
Dielectric Constant   4.1
@Frequency 1.00e+6 Hz		 4.1
@Frequency 1.00e+6 Hz		 IEC 60250
  4.2
@Frequency 100 Hz		 4.2
@Frequency 100 Hz		 IEC 60250
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  158 °C 316 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  90.0 °C 194 °F ISO 75-1/-2
Vicat Softening Point  160 °C 320 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Flame Spread  28 mm/min
@Thickness 1.00 mm		 1.1 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >POM< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM ISO 1043
UL recognition UL  
  UL
图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-38490.html

免责声明: 本文 杜邦高性能聚合物聚甲醛POM 500cl NC010 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4