类别：聚合物；热塑性；聚甲醛（POM）
材料说明：®M50是挤压和比通用级高韧性良好的加工性能中等粘度注塑级。
建议与长度至少20:1的直径比标准挤出机。螺钉应至少3:1和4:1的高压缩比的最好保证良好的熔融和熔体的均匀性。设计应约35%每层
特性：可加工性良好 韧性良好 中等粘性。物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 | ||
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.75 % | 0.75 % | ISO 62 | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.022 cm/cm | 0.022 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ASTM D955 | ||
| Melt Flow | 4.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
(MVR) cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | ASTM D638 | ||
| 63.0 MPa | 9140 psi | 50mm/min; ISO 527-2/1A | |||
| 34.5 MPa @Temperature 71.1 °C |
5000 psi @Temperature 160 °F |
ASTM D638 | |||
| 94.5 MPa @Temperature -40.0 °C |
13700 psi @Temperature -40.0 °F |
ASTM D638 | |||
| Elongation at Yield | 12 % | 12 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.50 GPa | 363 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 | ||
| 0.689 GPa @Temperature 104 °C |
100 ksi @Temperature 220 °F |
ASTM D790 | |||
| 1.24 GPa @Temperature 71.1 °C |
180 ksi @Temperature 160 °F |
ASTM D790 | |||
| 2.59 GPa @Temperature 22.8 °C |
375 ksi @Temperature 73.0 °F |
ASTM D790 | |||
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | ASTM D256 | ||
| 0.587 J/cm @Temperature -40.0 °C |
1.10 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |||
| Izod Impact, Notched (ISO) | 7.50 kJ/m² | 3.57 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 165 °C | 329 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75-1, -2 | ||
| 110 °C | 230 °F | ASTM D648 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | ||
| Zone 1 | 170 - 180 °C | 338 - 356 °F | |||
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 3 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 4 | 190 - 200 °C | 374 - 392 °F | |||
| Die Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Melt Temperature | 160 - 220 °C | 320 - 428 °F | |||
| Mold Temperature | 82.2 - 93.3 °C | 180 - 200 °F | generally preferred range, may vary with thickness | ||
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Dry Time | 3.00 hour | 3.00 hour | |||
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Hold Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Back Pressure | 0.500 MPa | 72.5 psi | |||
| Hot-Working Temperature | 180 - 200 °C | 356 - 392 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | slow-medium | ||||
| Pellets | Yes | ||||
| Pre-drying | Drying is not normally required with proper storage | ||||
| Processing conditions | ISO 9988-2 | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com