类别：聚合物；热塑性；聚甲醛（POM）；共聚甲醛，30%玻璃纤维增强
材料说明：30%玻璃珠注塑级，低翘曲的部位，滑改性聚四氟乙烯
玻璃珠+聚四氟乙烯
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 | ||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
(MVR) cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 50mm/min; ISO 527-2/1A | ||
| Elongation at Break | 13 % | 13 % | 50mm/min; ISO 527-2/1A | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 3.80 GPa | 551 ksi | 1mm/min; ISO 527-2/1A | ||
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 166 °C | 331 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | |||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Processing conditions | ISO 9988-2 | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com