| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D 792 |
| 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.021 cm/cm @Time 86400 sec |
0.021 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0214 cm/cm @Time 86400 sec |
0.0214 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0205 cm/cm @Time 86400 sec |
0.0205 in/in @Time 24.0 hour |
ISO 294 |
| 0.021 cm/cm @Time 86400 sec |
0.021 in/in @Time 24.0 hour |
ASTM D 955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527 |
| 50.0 MPa | 7250 psi | ASTM D 638 | |
| Elongation at Break | 10.5 % | 10.5 % | ISO 527 |
| 12.5 % | 12.5 % | ASTM D 638 | |
| Tensile Modulus | 2.20 GPa | 319 ksi | 50 mm/min; ASTM D 638 |
| 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D 790 |
| 77.0 MPa | 11200 psi | ISO 178 | |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D 790 |
| 2.80 GPa | 406 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.27 J/cm @Temperature 23.0 °C |
8.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² @Temperature 23.0 °C |
13.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.16 | 0.16 | ASTM D 3702 Modified |
| K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM-KP004AXZ 图：