| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D 638 |
| Elongation at Break | 3.1 % | 3.1 % | ASTM D 638 |
| Tensile Modulus | 5.08 GPa | 737 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D 790 |
| Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.580 J/cm @Temperature 23.0 °C |
1.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.07 J/cm @Temperature 23.0 °C |
9.50 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM-KFL22 图：