| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D 792 |
| Density | 1.65 g/cc | 0.0596 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.22 % | 0.22 % | 23°C / 50% RH; ISO 62 |
| 0.14 % @Time 86400 sec |
0.14 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
| 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
| 38.0 MPa | 5510 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 7.0 % | 7.0 % | 5 mm/min; ISO 527 |
| 8.0 % | 8.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 3.5 % | 3.5 % | Type I, 5 mm/min; ASTM D 638 |
| 3.5 % | 3.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.22 GPa | 467 ksi | 1 mm/min; ISO 527 |
| 3.35 GPa | 486 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.91 GPa | 422 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.96 GPa | 429 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.400 J/cm @Temperature 23.0 °C |
0.749 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.47 J/cm @Temperature 23.0 °C |
6.50 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² @Temperature 23.0 °C |
9.04 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.43 | 0.43 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.49 | 0.49 | ASTM D 3702 Modified |
| K (wear) Factor | 10.1 x 10-8 mm³/N-M | 5.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D 3702 Modified |
| 322 x 10-8 mm³/N-M | 160 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 87.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
48.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 91.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 90.0 °C @Thickness 3.20 mm |
194 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM-KZL34 图：