| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D 792 |
| 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 1.8 % @Time 86400 sec |
1.8 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.020 - 0.024 cm/cm @Time 86400 sec |
0.020 - 0.024 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.020 - 0.024 cm/cm @Time 86400 sec |
0.020 - 0.024 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.019 - 0.024 cm/cm @Time 86400 sec |
0.019 - 0.024 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.019 - 0.024 cm/cm @Time 86400 sec |
0.019 - 0.024 in/in @Time 24.0 hour |
ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D 638 |
| 43.0 MPa | 6240 psi | ISO 527 | |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D 638 |
| 48.0 MPa | 6960 psi | ISO 527 | |
| Elongation at Break | 28.6 % | 28.6 % | ISO 527 |
| 48 % | 48 % | ASTM D 638 | |
| Elongation at Yield | 12 % | 12 % | ASTM D 638 |
| 12.1 % | 12.1 % | ISO 527 | |
| Tensile Modulus | 1.82 GPa | 264 ksi | 50 mm/min; ASTM D 638 |
| 1.97 GPa | 286 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D 790 |
| 63.0 MPa | 9140 psi | ISO 178 | |
| Flexural Modulus | 1.66 GPa | 241 ksi | ASTM D 790 |
| 1.75 GPa | 254 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm @Temperature 23.0 °C |
2.19 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 16.82 J/cm @Temperature 23.0 °C |
31.51 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 130 kJ/m² @Temperature 23.0 °C |
61.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 23.0 J @Temperature 23.0 °C |
17.0 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+10 - 1.00e+11 ohm-cm | 1.00e+10 - 1.00e+11 ohm-cm | ASTM D 257 |
| Surface Resistance | 1.00e+10 - 1.00e+11 ohm | 1.00e+10 - 1.00e+11 ohm | ASTM D 257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 150 °C @Thickness 3.20 mm |
302 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 77.0 °C @Thickness 3.20 mm |
171 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM-K3000 图：