类别：聚合物；热塑性；聚甲醛（POM）；乙缩醛共聚物，无筋
材料说明：Hostaform®缩醛共聚物是一种强度高，结晶，热塑性工程树脂的平衡性能和易加工性能提供性能和成本比其他材料的优点。
这个等级的具体说明：这是在代码级的Hostaform XAP，为创新发展先进的加工产品和AP X站。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.20 % @Temperature 23.0 °C |
0.20 % @Temperature 73.4 °F |
80x80x1mm, 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.65 % @Temperature 23.0 °C |
0.65 % @Temperature 73.4 °F |
80x80x1 mm; ISO 62 | ||
| Melt Flow | 16.92 g/10 min @Load 2.16 kg, Temperature 190 °C |
16.92 g/10 min @Load 4.76 lb, Temperature 374 °F |
Calculated from Volume flow Rate: 12 cm3/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 143 MPa | 20700 psi | 30 sec value, 20x20x4 mm; ISO 2039, part 1; applied load 358 N | ||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min | ||
| Elongation at Break | 25 % | 25 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min | ||
| Elongation at Yield | 9.0 % | 9.0 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min | ||
| Tensile Modulus | 2.90 GPa | 421 ksi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 1 mm/min | ||
| Flexural Modulus | 2.80 GPa | 406 ksi | 80x10x4mm from multi-purpose test specimen (ISO 3167); ISO 178 | ||
| Charpy Impact Unnotched | 14.0 J/cm² @Temperature -30.0 °C |
66.6 ft-lb/in² @Temperature -22.0 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU | ||
| 15.0 J/cm² @Thickness 4.00 mm, Temperature 23.0 °C |
71.4 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA | ||
| 0.600 J/cm² @Thickness 4.00 mm, Temperature 23.0 °C |
2.86 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA | |||
| Tensile Creep Modulus, 1 hour | 2500 MPa | 363000 psi | multi-purpose test specimen (ISO 3167); ISO 899, part 1 | ||
| Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | multi-purpose test specimen (ISO 3167); ISO 899, part 1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
80x80x1 mm; IEC 60250 | ||
| 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
80x80x1 mm; IEC 60250 | |||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | 80x80x1 mm; IEC 60243, part 1 | ||
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
80x80x1 mm; IEC 60250 | ||
| 0.0050 @Frequency 1e+6 Hz |
0.0050 @Frequency 1e+6 Hz |
80x80x1 mm; IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
Longitudinal, 30x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 11359, part 1/2 | ||
| Melting Point | 166 °C | 331 °F | DSC, 10 K/min, Molding compound; ISO 3146, method C1b | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | 80x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 75, part 1/2 | ||
| Vicat Softening Point | 151 °C | 304 °F | VST/B/50, 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 306 | ||
| De |
|||||
| Emission | Max 10 mg/kg | VDA 275 (Molded plate 1.5 mm) |
|||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com