| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.023 - 0.027 cm/cm | 0.023 - 0.027 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0235 - 0.0275 cm/cm | 0.0235 - 0.0275 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 35.0 MPa | 5080 psi | |||
| Elongation at Break | >= 100 % @Temperature 60.0 °C |
>= 100 % @Temperature 140 °F |
|||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||||
| 100 % @Temperature 23.0 °C |
100 % @Temperature 73.4 °F |
||||
| Tensile Modulus | 0.500 GPa @Temperature 90.0 °C |
72.5 ksi @Temperature 194 °F |
|||
| 0.900 GPa @Temperature 60.0 °C |
131 ksi @Temperature 140 °F |
||||
| 1.50 GPa @Temperature 23.0 °C |
218 ksi @Temperature 73.4 °F |
||||
| Charpy Impact Unnotched | NB | NB | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 65.0 °C | 149 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |||
| Vicat Softening Point | 125 °C @Load 5.00 kg |
257 °F @Load 11.0 lb |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 175 - 200 °C | 347 - 392 °F | |||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |||
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
|||
| De |
|||||
| ISO Shrinkage - Pressure | 60 MPa | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com