| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | |||
| Elongation at Break | 85 % | 85 % | |||
| Elongation at Yield | 8.0 % | 8.0 % | |||
| Tensile Modulus | 1.70 GPa | 247 ksi | |||
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | |||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | 260 ohm | 260 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 °C | 104 °F | |||
| Vicat Softening Point | 125 °C @Load 5.00 kg |
257 °F @Load 11.0 lb |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Drying Temperature | 70.0 - 90.0 °C @Time 10800 sec |
158 - 194 °F @Time 3.00 hour |
|||
| De |
|||||
| ISO Shrinkage - Pressure | 60 MPa | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com