| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 | ||
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 1.25 % | 1.25 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | ||
| Melt Flow | 9.7 g/10 min @Load 6.60 kg, Temperature 337 °C |
9.7 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 | ||
| Melt Index of Compound | 13 g/10 min @Load 5.00 kg, Temperature 220 °C |
13 g/10 min @Load 11.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 | ||
| 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 | |||
| Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 | ||
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 | |||
| Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D638 | ||
| 60 % | 60 % | 5 mm/min; ISO 527 | |||
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 | ||
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | |||
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 | ||
| 3.58 GPa | 519 ksi | 5 mm/min; ASTM D638 | |||
| Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 | ||
| 173 MPa | 25100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |||
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 | ||
| 3.43 GPa | 497 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |||
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 | ||
| 0.550 J/cm @Temperature -30.0 °C |
1.03 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |||
| Izod Impact, Unnotched | 13.35 J/cm | 25.01 ft-lb/in | ASTM D4812 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A | ||
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.15 @Frequency 1000 Hz |
3.15 @Frequency 1000 Hz |
ASTM D150 | ||
| Dielectric Strength | 27.9 kV/mm @Thickness 1.60 mm |
709 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | ||
| 32.7 kV/mm @Thickness 1.60 mm |
831 kV/in @Thickness 0.0630 in |
in air; ASTM D149 | |||
| Dissipation Factor | 0.0013 @Frequency 1000 Hz |
0.0013 @Frequency 1000 Hz |
ASTM D150 | ||
| 0.0025 @Frequency 2.45e+9 Hz |
0.0025 @Frequency 2.45e+9 Hz |
ASTM D150 | |||
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 | ||
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A | ||
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A | ||
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | ||
| 55.8 µm/m-°C @Temperature -20.0 - 150 °C |
31.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | |||
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | ||
| 54.0 µm/m-°C @Temperature -20.0 - 150 °C |
30.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| 201 °C @Thickness 6.40 mm |
394 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |||
| Vicat Softening Point | 211 °C | 412 °F | Rate B/120; ISO 306 | ||
| 215 °C | 419 °F | Rate B/50; ISO 306 | |||
| 218 °C | 424 °F | Rate B/50; ASTM D1525 | |||
| Glass Transition Temp, Tg | 217 °C | 423 °F | |||
| UL RTI, Electrical | 170 °C | 338 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B | ||
| Flammability, UL94 | V-2 @Thickness 0.400 mm |
V-2 @Thickness 0.0157 in |
UL 94 | ||
| V-1 @Thickness 0.750 mm |
V-1 @Thickness 0.0295 in |
UL 94 | |||
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 | |||
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 | |||
| Oxygen Index | 47 % | 47 % | ASTM D2863 | ||
| De |
|||||
| NBS Smoke Density, Flaming, Ds 4 min | 0.7 | ASTM E 662 |
|||
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
PEI 1000RV 图：