| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 | ||
| Water Absorption | 0.25 % @Time 86400 sec |
0.25 % @Time 24.0 hour |
ASTM D570 | ||
| Moisture Absorption at Equilibrium | 1.25 % | 1.25 % | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | ||
| Melt Flow | 17.8 g/10 min @Load 6.60 kg, Temperature 337 °C |
17.8 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 109 | 109 | ASTM D785 | ||
| Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 | ||
| Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D638 | ||
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | ||
| Tensile Modulus | 3.58 GPa | 519 ksi | 5 mm/min; ASTM D638 | ||
| Flexural Yield Strength | 165 MPa | 23900 psi | 2.6 mm/min, 100 mm span; ASTM D790 | ||
| Flexural Modulus | 3.51 GPa | 509 ksi | 2.6 mm/min, 100 mm span; ASTM D790 | ||
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 | ||
| 11.74 J/cm @Thickness 3.20 mm |
21.99 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |||
| Izod Impact, Unnotched | 13.35 J/cm | 25.01 ft-lb/in | ASTM D4812 | ||
| Gardner Impact | 33.0 J | 24.3 ft-lb | ASTM D3029 | ||
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.15 @Frequency 1000 Hz |
3.15 @Frequency 1000 Hz |
ASTM D150 | ||
| Dielectric Strength | 27.9 kV/mm @Thickness 1.60 mm |
709 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | ||
| 32.6 kV/mm @Thickness 1.60 mm |
828 kV/in @Thickness 0.0630 in |
in air; ASTM D149 | |||
| Dissipation Factor | 0.0013 @Frequency 1000 Hz |
0.0013 @Frequency 1000 Hz |
ASTM D150 | ||
| 0.0025 @Frequency 2.45e+9 Hz |
0.0025 @Frequency 2.45e+9 Hz |
ASTM D150 | |||
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 | ||
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A | ||
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A | ||
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 55.8 µm/m-°C @Temperature -20.0 - 150 °C |
31.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | ||
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ASTM C177 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C @Thickness 6.40 mm |
405 °F @Thickness 0.252 in |
unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D648 | ||
| Vicat Softening Point | 218 °C | 424 °F | Rate B/50; ASTM D1525 | ||
| Glass Transition Temp, Tg | 217 °C | 423 °F | |||
| UL RTI, Electrical | 170 °C | 338 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 | ||
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 | |||
| Oxygen Index | 44 % | 44 % | ASTM D2863 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified | ||
| De |
|||||
| NBS Smoke Density, Flaming, Ds 4 min | 2 | ASTM E 662 |
|||
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
PEI 1010 图：