| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 63.5 MPa | 9210 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | 28 % | 28 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 6.2 % | 6.2 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 2.44 GPa | 354 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 2.28 GPa | 331 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | ISO Test | ||
| 12.0 kJ/m² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
ISO Test | |||
| Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | ISO 179 | ||
| 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C | 378 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 | ||
| De |
|||||
| Color | BK20465 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
聚酰胺俗称尼龙（Nylon），英文名称Polyamide（简称PA），是分子主链上含有重复酰胺基团—[NHCO]—的热塑性树脂总称。包括脂肪族PA，脂肪—芳香族PA和芳香族PA。其中，脂肪族PA品种多，产量大，应用广泛，其命名由合成单体具体的碳原子数而定。
下图仅供参考（非实物图）：
用途：
广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com