| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % @Time 86400 sec |
0.40 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 163 MPa | 23600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
17.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 96.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
53.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C | 322 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com