| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.7 - 7.7 % | 6.7 - 7.7 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.0 - 2.6 % | 2.0 - 2.6 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage | 0.0085 cm/cm | 0.0085 in/in | restricted | ||
| Melt Flow | 10.6 g/10 min @Load 5.00 kg, Temperature 275 °C |
10.6 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Break | 45 % | 45 % | Nominal, 50mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 5 % | 5 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 1.90 GPa | 276 ksi | ISO 527-1/-2 | ||
| Izod Impact, Notched (ISO) | 29.0 kJ/m² @Temperature -30.0 °C |
13.8 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | ||
| 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 3.10 J/cm² @Temperature -30.0 °C |
14.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1000 hours | 450 MPa @Strain <=0.500 % |
65300 psi @Strain <=0.500 % |
ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 4.00e+12 ohm-cm | 4.00e+12 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.1 @Frequency 1.00 Hz |
3.1 @Frequency 1.00 Hz |
IEC 60250 | ||
| Dissipation Factor | 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 70.0 - 100 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 - 55.6 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 | ||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 310 °C | >= 590 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 290 °C | 554 °F | Feed zone | ||
| Zone 2 | 290 °C | 554 °F | Compression | ||
| Zone 3 | 290 °C | 554 °F | Metering-zone | ||
| Zone 4 | 290 °C | 554 °F | Nozzle | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection-molding/Extrusion | ||
| 290 °C | 554 °F | Optimal | |||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection-molding | ||
| 60.0 °C | 140 °F | Optimal | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| De |
|||||
| Color | BK 30464 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||
PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。
下图仅供参考（非实物图）：
应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。