类别：聚合物；热塑性塑料；尼龙；尼龙6；尼龙6，50%玻璃纤维填充
材料说明：在tepex®复合材料层合板，聚酰胺6树脂以其韧性，硬度，耐磨性，耐热性和耐化学性。无碱玻璃纤维粗纱具有极好的抗冲击性能。这使得复合材料的坚韧和耐疲劳，同时提供优良的机械性能。
典型的应用环境是在汽车应用，大型结构件，保险杠系统，结构运动用品的应用，头盔外壳。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | |||
| Filler Content | 47 % | 47 % | by volume | ||
| Thickness | 500 microns | 19.7 mil | laminate layer thickness | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 390 MPa | 56600 psi | transverse; ISO 527-4/5 | ||
| 404 MPa | 58600 psi | longitudinal; ISO 527-4/5 | |||
| Elongation at Break | 2.2 % | 2.2 % | longitudinal; ISO 527-4/5 | ||
| 2.2 % | 2.2 % | transverse; ISO 527-4/5 | |||
| Tensile Modulus | 21.5 GPa | 3120 ksi | transverse; ISO 527-4/5 | ||
| 22.4 GPa | 3250 ksi | longitudinal; ISO 527-4/5 | |||
| Flexural Strength | 585 MPa | 84800 psi | transverse; ISO 178 | ||
| 620 MPa | 89900 psi | longitudinal; ISO 178 | |||
| Flexural Modulus | 18.7 GPa | 2710 ksi | transverse; ISO 178 | ||
| 19.2 GPa | 2780 ksi | longitudinal; ISO 178 | |||
| Poissons Ratio | 0.17 | 0.17 | longitudinal; ISO 527-4/5 | ||
| 0.17 | 0.17 | transverse; ISO 527-4/5 | |||
| Charpy Impact Unnotched | 14.5 J/cm² | 69.0 ft-lb/in² | longitudinal; ISO 179/1eU | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
8.33 µin/in-°F @Temperature 73.4 - 176 °F |
longitudinal; ASTM E831 | ||
| 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
8.33 µin/in-°F @Temperature 73.4 - 176 °F |
transverse; ASTM E831 | |||
| 19.0 µm/m-°C @Temperature -30.0 - 23.0 °C |
10.6 µin/in-°F @Temperature -22.0 - 73.4 °F |
longitudinal; ASTM E831 | |||
| 19.0 µm/m-°C @Temperature -30.0 - 23.0 °C |
10.6 µin/in-°F @Temperature -22.0 - 73.4 °F |
transverse; ASTM E831 | |||
| Melting Point | 220 °C | 428 °F | DSC 3146 | ||
| Maximum Service Temperature, Air | 120 °C @Time 7.20e+7 sec |
248 °F @Time 20000 hour |
Relative Temperature Index; IEC 216/1 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/2 | ||
| Minimum Service Temperature, Air | -30.0 °C | -22.0 °F | |||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | DSC 3146 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 240 - 260 °C | 464 - 500 °F | |||
| De |
|||||
| Reinforcement | Area weight | 600 g/m² | |||
| Fabric | twill | ||||
| Fibers | roving glass | ||||
| Weight Rate | 50% longitudinal and transverse | ||||
| Yarn | 1200 tex longitudinal and transverse |
||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com