类别：聚合物；热塑性塑料；尼龙；尼龙66；尼龙66，60%玻璃纤维填充
材料说明：说明：Ultramid hmg14 HS - 102是60%玻璃纤维增强PA66，提供高强度和刚度的注塑级。由于固有的较低的吸湿性，Ultramid hmg14 HS - 102显示改进的保持湿度调节后的力学性能。此外，成型零件具有特殊的表面光洁度。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 248 MPa | 36000 psi | ISO 527 | ||
| Elongation at Break | 2.2 % | 2.2 % | ISO 527 | ||
| Tensile Modulus | 20.2 GPa | 2930 ksi | ISO 527 | ||
| Flexural Strength | 383 MPa | 55500 psi | ISO 178 | ||
| Flexural Modulus | 18.9 GPa | 2740 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180 | ||
| 13.0 kJ/m² | 6.19 ft-lb/in² | ISO 180 | |||
| Charpy Impact Unnotched | 9.50 J/cm² @Temperature -30.0 °C |
45.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | ||
| 9.90 J/cm² @Temperature 23.0 °C |
47.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |||
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | ||
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 305 °C | 536 - 581 °F | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.12 % | <= 0.12 % | |||
| De |
|||||
| Color | BK 102 | ||||
| Commercial Status | North America | ||||
应用：Ultramid hmg14 HS - 102是专为需要高刚度的应用和应被视为是由金属部件。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。