  4. 杜邦高性能聚合物RS lc4601 NC010尼龙

杜邦高性能聚合物RS lc4601 NC010尼龙

杜邦高性能聚合物Zytel®RS lc4601 NC010尼龙 类别：聚合物；热塑性塑料；尼龙 材料说明：增塑增韧聚酰胺开发可再生来源的挤压 Zytel RS lc4601 NC010是一个灵活的增韧增塑聚酰胺树脂用于挤出应用。
物性表：

 
Physical Properties Metric English Comments
Density  1.04 g/cc 0.0376 lb/in³ DAM; ISO 1183
Moisture Absorption  1.00 %
@Thickness 2.00 mm		 1.00 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
 
Mechanical Properties Metric English Comments
Tensile Stress   0.260 MPa
@Strain 0.200 %,
Temperature 150 °C		 37.7 psi
@Strain 0.200 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  0.270 MPa
@Strain 0.230 %,
Temperature 150 °C		 39.2 psi
@Strain 0.230 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  0.350 MPa
@Strain 0.210 %,
Temperature 90.0 °C		 50.8 psi
@Strain 0.210 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  0.390 MPa
@Strain 0.230 %,
Temperature 90.0 °C		 56.6 psi
@Strain 0.230 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  0.510 MPa
@Strain 0.210 %,
Temperature 40.0 °C		 74.0 psi
@Strain 0.210 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  2.00 MPa
@Strain 0.310 %,
Temperature 23.0 °C		 290 psi
@Strain 0.310 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.32 MPa
@Strain 4.49 %,
Temperature 150 °C		 482 psi
@Strain 4.49 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  3.37 MPa
@Strain 0.220 %,
Temperature 0.000 °C		 489 psi
@Strain 0.220 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  3.95 MPa
@Strain 0.220 %,
Temperature 0.000 °C		 573 psi
@Strain 0.220 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  4.74 MPa
@Strain 0.240 %,
Temperature -40.0 °C		 687 psi
@Strain 0.240 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  4.76 MPa
@Strain 0.240 %,
Temperature -40.0 °C		 690 psi
@Strain 0.240 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  4.82 MPa
@Strain 10.44 %,
Temperature 150 °C		 699 psi
@Strain 10.44 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  5.73 MPa
@Strain 14.35 %,
Temperature 150 °C		 831 psi
@Strain 14.35 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  5.80 MPa
@Strain 20.99 %,
Temperature 150 °C		 841 psi
@Strain 20.99 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  5.96 MPa
@Strain 1.19 %,
Temperature 40.0 °C		 864 psi
@Strain 1.19 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  6.16 MPa
@Strain 30.21 %,
Temperature 150 °C		 893 psi
@Strain 30.21 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  6.20 MPa
@Strain 5.39 %,
Temperature 90.0 °C		 899 psi
@Strain 5.39 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  6.70 MPa
@Strain 0.520 %,
Temperature 23.0 °C		 972 psi
@Strain 0.520 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  6.71 MPa
@Strain 28.97 %,
Temperature 150 °C		 973 psi
@Strain 28.97 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  7.09 MPa
@Strain 7.59 %,
Temperature 90.0 °C		 1030 psi
@Strain 7.59 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  9.50 MPa
@Strain 6.34 %,
Temperature 40.0 °C		 1380 psi
@Strain 6.34 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  9.60 MPa
@Strain 13.16 %,
Temperature 90.0 °C		 1390 psi
@Strain 13.16 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  10.39 MPa
@Strain 21.62 %,
Temperature 90.0 °C		 1507 psi
@Strain 21.62 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  11.39 MPa
@Strain 24.79 %,
Temperature 90.0 °C		 1652 psi
@Strain 24.79 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  11.78 MPa
@Strain 43.21 %,
Temperature 90.0 °C		 1709 psi
@Strain 43.21 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  13.92 MPa
@Strain 15.49 %,
Temperature 40.0 °C		 2019 psi
@Strain 15.49 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  16.46 MPa
@Strain 29.92 %,
Temperature 40.0 °C		 2387 psi
@Strain 29.92 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  18.4 MPa
@Strain 12.09 %,
Temperature 40.0 °C		 2670 psi
@Strain 12.09 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  21.67 MPa
@Strain 26.87 %,
Temperature 40.0 °C		 3143 psi
@Strain 26.87 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  23.2 MPa
@Strain 45.66 %,
Temperature 40.0 °C		 3360 psi
@Strain 45.66 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  23.81 MPa
@Strain 25.97 %,
Temperature 23.0 °C		 3453 psi
@Strain 25.97 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  24.96 MPa
@Strain 1.36 %,
Temperature -40.0 °C		 3620 psi
@Strain 1.36 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  25.3 MPa
@Strain 1.36 %,
Temperature -40.0 °C		 3670 psi
@Strain 1.36 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  33.08 MPa
@Strain 2.19 %,
Temperature 0.000 °C		 4798 psi
@Strain 2.19 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  36.4 MPa
@Strain 4.17 %,
Temperature 0.000 °C		 5280 psi
@Strain 4.17 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  38.89 MPa
@Strain 12.77 %,
Temperature 0.000 °C		 5641 psi
@Strain 12.77 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  45.72 MPa
@Strain 2.83 %,
Temperature -40.0 °C		 6631 psi
@Strain 2.83 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  46.01 MPa
@Strain 2.73 %,
Temperature -40.0 °C		 6673 psi
@Strain 2.73 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  48.45 MPa
@Strain 6.05 %,
Temperature 0.000 °C		 7027 psi
@Strain 6.05 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  55.63 MPa
@Strain 4.13 %,
Temperature -40.0 °C		 8068 psi
@Strain 4.13 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  60.25 MPa
@Strain 4.21 %,
Temperature -40.0 °C		 8739 psi
@Strain 4.21 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Tensile Modulus  0.750 GPa 109 ksi DAM; ISO 527-1/-2
Flexural Modulus  0.700 GPa 102 ksi DAM; ISO 178
Secant Modulus   0.0333 GPa
@Strain 34.93 %,
Temperature 100 °C		 4.82 ksi
@Strain 34.93 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.0362 GPa
@Strain 49.84 %,
Temperature 40.0 °C		 5.25 ksi
@Strain 49.84 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  0.0425 GPa
@Strain 23.28 %,
Temperature 100 °C		 6.17 ksi
@Strain 23.28 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.0674 GPa
@Strain 13.79 %,
Temperature 100 °C		 9.77 ksi
@Strain 13.79 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.0729 GPa
@Strain 30.23 %,
Temperature 40.0 °C		 10.6 ksi
@Strain 30.23 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  0.0790 GPa
@Strain 18.63 %,
Temperature 40.0 °C		 11.5 ksi
@Strain 18.63 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  0.0815 GPa
@Strain 8.86 %,
Temperature 100 °C		 11.8 ksi
@Strain 8.86 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.0917 GPa
@Strain 25.97 %,
Temperature 23.0 °C		 13.3 ksi
@Strain 25.97 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  0.116 GPa
@Strain 4.58 %,
Temperature 100 °C		 16.8 ksi
@Strain 4.58 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.150 GPa
@Strain 6.34 %,
Temperature 40.0 °C		 21.7 ksi
@Strain 6.34 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  0.152 GPa
@Strain 12.09 %,
Temperature 40.0 °C		 22.1 ksi
@Strain 12.09 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  0.170 GPa
@Strain 0.200 %,
Temperature 100 °C		 24.7 ksi
@Strain 0.200 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  0.180 GPa
@Strain 0.200 %,
Temperature 100 °C		 26.1 ksi
@Strain 0.200 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  0.243 GPa
@Strain 0.210 %,
Temperature 40.0 °C		 35.2 ksi
@Strain 0.210 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  0.50084 GPa
@Strain 1.19 %,
Temperature 40.0 °C		 72.642 ksi
@Strain 1.19 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  0.645 GPa
@Strain 0.310 %,
Temperature 23.0 °C		 93.6 ksi
@Strain 0.310 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  0.780 GPa
@Strain 7.93 %,
Temperature -40.0 °C		 113 ksi
@Strain 7.93 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  0.873 GPa
@Strain 4.17 %,
Temperature 0.000 °C		 127 ksi
@Strain 4.17 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  0.966 GPa
@Strain 6.93 %,
Temperature -40.0 °C		 140 ksi
@Strain 6.93 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  1.15 GPa
@Strain 5.13 %,
Temperature -40.0 °C		 168 ksi
@Strain 5.13 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  1.27 GPa
@Strain 5.06 %,
Temperature -40.0 °C		 184 ksi
@Strain 5.06 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  1.29 GPa
@Strain 0.520 %,
Temperature 23.0 °C		 187 ksi
@Strain 0.520 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  1.5105 GPa
@Strain 2.19 %,
Temperature 0.000 °C		 219.08 ksi
@Strain 2.19 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  1.53 GPa
@Strain 3.25 %,
Temperature -40.0 °C		 221 ksi
@Strain 3.25 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  1.53 GPa
@Strain 0.220 %,
Temperature 0.000 °C		 222 ksi
@Strain 0.220 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  1.57 GPa
@Strain 3.44 %,
Temperature -40.0 °C		 228 ksi
@Strain 3.44 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  1.80 GPa
@Strain 0.220 %,
Temperature 0.000 °C		 260 ksi
@Strain 0.220 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  1.84 GPa
@Strain 1.36 %,
Temperature -40.0 °C		 266 ksi
@Strain 1.36 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  1.86 GPa
@Strain 1.36 %,
Temperature -40.0 °C		 270 ksi
@Strain 1.36 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  1.975 GPa
@Strain 0.240 %,
Temperature -40.0 °C		 286.5 ksi
@Strain 0.240 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  1.98 GPa
@Strain 0.240 %,
Temperature -40.0 °C		 288 ksi
@Strain 0.240 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  75.0 kJ/m² 35.7 ft-lb/in² DAM; ISO 180/1A
  15.0 kJ/m²
@Temperature -40.0 °C		 7.14 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
Charpy Impact Unnotched  NB NB DAM; ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 DAM; ISO 179/1eU
Charpy Impact, Notched  9.50 J/cm² 45.2 ft-lb/in² DAM; partial; ISO 179/1eA
  1.50 J/cm²
@Temperature -40.0 °C		 7.14 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
 
Thermal Properties Metric English Comments
Melting Point  214 °C 417 °F DAM; 10°C/min; ISO 11357-1/-3
Glass Transition Temp, Tg  50.0 °C 122 °F DAM; 10°C/min; ISO 11357-1/-2
 
Descriptive Properties
Additives Plasticiser  
Delivery form Pellets  
Part Marking Code >PA-IP< ISO 11469
Processing Other Extrusion  
  Profile Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA-IP ISO 1043
Special characteristics Heat stabilised or stable to heat
图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39667.html

免责声明: 本文 杜邦高性能聚合物RS lc4601 NC010尼龙 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4