  4. PA66/美国杜邦/70G13L NC010 增强级 耐高温

PA66/美国杜邦/70G13L NC010 增强级 耐高温

PA66/美国杜邦/70G13L NC010注塑级 增强级 耐高温
 参考图片：

颗粒图片：

包装图片：

成品图片：
100001041143_13526462585748

 

 

 
Physical Properties Metric English Comments
Density  1.23 g/cc 0.0444 lb/in³ DAM; ISO 1183
Water Absorption  7.6 %
@Thickness 2.00 mm		 7.6 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  2.20 %
@Thickness 2.00 mm		 2.20 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Water Absorption at Saturation  1.7 % 1.7 % DAM; Immersion 24h; ASTM D570
Viscosity Test  150 cm³/g 150 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0070 cm/cm 0.0070 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.012 cm/cm 0.012 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  75.0 MPa 10900 psi 50%RH; ISO 527-1/-2
  120 MPa 17400 psi DAM; ISO 527-1/-2
Tensile Stress   16.074 MPa
@Strain 0.500 %,
Temperature 23.0 °C		 2331.3 psi
@Strain 0.500 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  25.09 MPa
@Strain 0.500 %,
Temperature 23.0 °C		 3639 psi
@Strain 0.500 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  27.636 MPa
@Strain 0.900 %,
Temperature 23.0 °C		 4008.3 psi
@Strain 0.900 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  28.1 MPa
@Strain 0.500 %,
Temperature 0.000 °C		 4080 psi
@Strain 0.500 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  31.4 MPa
@Strain 0.500 %,
Temperature -40.0 °C		 4550 psi
@Strain 0.500 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  32.8 MPa
@Strain 0.500 %,
Temperature -40.0 °C		 4760 psi
@Strain 0.500 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  41.172 MPa
@Strain 1.50 %,
Temperature 23.0 °C		 5971.5 psi
@Strain 1.50 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  50.6 MPa
@Strain 0.900 %,
Temperature 0.000 °C		 7340 psi
@Strain 0.900 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  57.7 MPa
@Strain 1.10 %,
Temperature 0.000 °C		 8370 psi
@Strain 1.10 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  58.02 MPa
@Strain 1.20 %,
Temperature 23.0 °C		 8415 psi
@Strain 1.20 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  59.314 MPa
@Strain 2.60 %,
Temperature 23.0 °C		 8602.8 psi
@Strain 2.60 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  61.9 MPa
@Strain 1.00 %,
Temperature -40.0 °C		 8980 psi
@Strain 1.00 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  66.8 MPa
@Strain 1.20 %,
Temperature 0.000 °C		 9690 psi
@Strain 1.20 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  73.8 MPa
@Strain 1.50 %,
Temperature 0.000 °C		 10700 psi
@Strain 1.50 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  74.8 MPa
@Strain 1.20 %,
Temperature -40.0 °C		 10800 psi
@Strain 1.20 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  76.234 MPa
@Strain 7.00 %,
Temperature 23.0 °C		 11057 psi
@Strain 7.00 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  78.4 MPa
@Strain 1.30 %,
Temperature -40.0 °C		 11400 psi
@Strain 1.30 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  79.3 MPa
@Strain 1.70 %,
Temperature 23.0 °C		 11500 psi
@Strain 1.70 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  86.5 MPa
@Strain 1.60 %,
Temperature 0.000 °C		 12500 psi
@Strain 1.60 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  89.0 MPa
@Strain 2.00 %,
Temperature 0.000 °C		 12900 psi
@Strain 2.00 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  94.05 MPa
@Strain 2.10 %,
Temperature 23.0 °C		 13640 psi
@Strain 2.10 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  98.5 MPa
@Strain 1.70 %,
Temperature -40.0 °C		 14300 psi
@Strain 1.70 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  99.8 MPa
@Strain 1.90 %,
Temperature 0.000 °C		 14500 psi
@Strain 1.90 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  100.6 MPa
@Strain 1.70 %,
Temperature -40.0 °C		 14590 psi
@Strain 1.70 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  119.91 MPa
@Strain 3.10 %,
Temperature 23.0 °C		 17392 psi
@Strain 3.10 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  121 MPa
@Strain 4.50 %,
Temperature 0.000 °C		 17500 psi
@Strain 4.50 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  127.2 MPa
@Strain 2.30 %,
Temperature -40.0 °C		 18450 psi
@Strain 2.30 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Elongation at Break  3.0 % 3.0 % DAM; ISO 527-1/-2
  13 % 13 % 50%RH; ISO 527-1/-2
Tensile Modulus  3.50 GPa 508 ksi 50%RH; ISO 527-1/-2
  5.50 GPa 798 ksi DAM; ISO 527-1/-2
Flexural Strength  100 MPa 14500 psi 50%RH; ISO 178
  190 MPa 27600 psi DAM; ISO 178
Flexural Modulus  2.90 GPa 421 ksi 50%RH; ISO 178
  4.80 GPa 696 ksi DAM; ISO 178
Secant Modulus   0.833 GPa
@Strain 6.00 %,
Temperature 80.0 °C		 121 ksi
@Strain 6.00 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  0.927 GPa
@Strain 7.50 %,
Temperature 80.0 °C		 134 ksi
@Strain 7.50 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.22 GPa
@Strain 3.70 %,
Temperature 80.0 °C		 177 ksi
@Strain 3.70 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.5125 GPa
@Strain 4.00 %,
Temperature 80.0 °C		 219.37 ksi
@Strain 4.00 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.58 GPa
@Strain 2.10 %,
Temperature 80.0 °C		 229 ksi
@Strain 2.10 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.70 GPa
@Strain 4.40 %,
Temperature 23.0 °C		 246 ksi
@Strain 4.40 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  1.86 GPa
@Strain 2.30 %,
Temperature 80.0 °C		 269 ksi
@Strain 2.30 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.88 GPa
@Strain 0.900 %,
Temperature 80.0 °C		 272 ksi
@Strain 0.900 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  1.94 GPa
@Strain 0.500 %,
Temperature 80.0 °C		 281 ksi
@Strain 0.500 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2.09 GPa
@Strain 3.20 %,
Temperature 23.0 °C		 302 ksi
@Strain 3.20 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.27 GPa
@Strain 1.00 %,
Temperature 80.0 °C		 329 ksi
@Strain 1.00 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  2.42 GPa
@Strain 0.500 %,
Temperature 80.0 °C		 351 ksi
@Strain 0.500 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  2.65 GPa
@Strain 1.70 %,
Temperature 23.0 °C		 384 ksi
@Strain 1.70 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.07 GPa
@Strain 0.900 %,
Temperature 23.0 °C		 445 ksi
@Strain 0.900 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.2148 GPa
@Strain 0.500 %,
Temperature 23.0 °C		 466.27 ksi
@Strain 0.500 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.35 GPa
@Strain 3.40 %,
Temperature 0.000 °C		 486 ksi
@Strain 3.40 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.008 GPa
@Strain 2.50 %,
Temperature 0.000 °C		 581.3 ksi
@Strain 2.50 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.07 GPa
@Strain 2.80 %,
Temperature 23.0 °C		 590 ksi
@Strain 2.80 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.37 GPa
@Strain 2.30 %,
Temperature 23.0 °C		 634 ksi
@Strain 2.30 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.58 GPa
@Strain 1.90 %,
Temperature 23.0 °C		 664 ksi
@Strain 1.90 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.74 GPa
@Strain 1.70 %,
Temperature 0.000 °C		 688 ksi
@Strain 1.70 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.835 GPa
@Strain 1.20 %,
Temperature 23.0 °C		 701.3 ksi
@Strain 1.20 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.018 GPa
@Strain 0.500 %,
Temperature 23.0 °C		 727.8 ksi
@Strain 0.500 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.04 GPa
@Strain 2.30 %,
Temperature 0.000 °C		 732 ksi
@Strain 2.30 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.232 GPa
@Strain 2.50 %,
Temperature -40.0 °C		 758.8 ksi
@Strain 2.50 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  5.25 GPa
@Strain 1.10 %,
Temperature 0.000 °C		 761 ksi
@Strain 1.10 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.36 GPa
@Strain 1.70 %,
Temperature 0.000 °C		 777 ksi
@Strain 1.70 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.57 GPa
@Strain 1.20 %,
Temperature 0.000 °C		 807 ksi
@Strain 1.20 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.575 GPa
@Strain 2.00 %,
Temperature -40.0 °C		 808.6 ksi
@Strain 2.00 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  5.62 GPa
@Strain 0.500 %,
Temperature 0.000 °C		 815 ksi
@Strain 0.500 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.62 GPa
@Strain 0.900 %,
Temperature 0.000 °C		 815 ksi
@Strain 0.900 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.81 GPa
@Strain 1.90 %,
Temperature -40.0 °C		 842 ksi
@Strain 1.90 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.91 GPa
@Strain 1.50 %,
Temperature -40.0 °C		 857 ksi
@Strain 1.50 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  6.19 GPa
@Strain 1.00 %,
Temperature -40.0 °C		 898 ksi
@Strain 1.00 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  6.23 GPa
@Strain 1.20 %,
Temperature -40.0 °C		 904 ksi
@Strain 1.20 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  6.28 GPa
@Strain 0.500 %,
Temperature -40.0 °C		 911 ksi
@Strain 0.500 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  6.56 GPa
@Strain 0.500 %,
Temperature -40.0 °C		 951 ksi
@Strain 0.500 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Izod Impact, Notched (ISO)  4.00 kJ/m² 1.90 ft-lb/in² 50%RH; ISO 180/1A
  4.50 kJ/m² 2.14 ft-lb/in² DAM; ISO 180/1A
  3.00 kJ/m²
@Temperature -30.0 °C		 1.43 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
  3.00 kJ/m²
@Temperature -40.0 °C		 1.43 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 180/1A
  4.50 kJ/m²
@Temperature -40.0 °C		 2.14 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
  4.50 kJ/m²
@Temperature -30.0 °C		 2.14 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  40.0 kJ/m² 19.0 ft-lb/in² DAM; ISO 180/1U
  55.0 kJ/m² 26.2 ft-lb/in² 50%RH; ISO 180/1U
  28.0 kJ/m²
@Temperature -30.0 °C		 13.3 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1U
  35.0 kJ/m²
@Temperature -30.0 °C		 16.7 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1U
Charpy Impact Unnotched  4.00 J/cm² 19.0 ft-lb/in² DAM; ISO 179/1eU
  7.00 J/cm² 33.3 ft-lb/in² 50%RH; ISO 179/1eU
  3.00 J/cm²
@Temperature -30.0 °C		 14.3 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
  4.00 J/cm²
@Temperature -30.0 °C		 19.0 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
Charpy Impact, Notched  0.500 J/cm² 2.38 ft-lb/in² DAM; ISO 179/1eA
  0.600 J/cm² 2.86 ft-lb/in² 50%RH; ISO 179/1eA
  0.400 J/cm²
@Temperature -40.0 °C		 1.90 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
  0.450 J/cm²
@Temperature -40.0 °C		 2.14 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
  0.450 J/cm²
@Temperature -30.0 °C		 2.14 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour  3300 MPa
@Time 3600 sec		 479000 psi
@Time 1.00 hour		 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours  2200 MPa
@Time 3.60e+6 sec		 319000 psi
@Time 1000 hour		 50%RH; ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm DAM; IEC 60093
Surface Resistance  1.00e+15 ohm 1.00e+15 ohm 50%RH; IEC 60093
Dielectric Constant   3.2
@Frequency 1.00e+6 Hz		 3.2
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
  3.9
@Frequency 100 Hz		 3.9
@Frequency 100 Hz		 DAM; IEC 60250
Dielectric Strength  25.0 kV/mm 635 kV/in DAM; IEC 60243-1
Dissipation Factor   0.013
@Frequency 100 Hz		 0.013
@Frequency 100 Hz		 DAM; IEC 60250
  0.015
@Frequency 1.00e+6 Hz		 0.015
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  40.0 µm/m-°C 22.2 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  96.0 µm/m-°C 53.3 µin/in-°F DAM; ISO 11359-1/-2
Melting Point  262 °C 504 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  258 °C 496 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  238 °C 460 °F DAM; ISO 75-1/-2
Vicat Softening Point  205 °C 401 °F DAM; 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  80.0 °C 176 °F DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 0.700 mm		 HB
@Thickness 0.0276 in		 DAM; IEC 60695-11-10
Flame Spread  27 mm/min
@Thickness 1.00 mm		 1.1 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  24 % 24 % DAM; ISO 4589-1/-2
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Emission of organic compounds 6 µgC/g VDA 277
Part Marking Code >PA66-GF13< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA66-GF13  

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39787.html

免责声明: 本文 PA66/美国杜邦/70G13L NC010 增强级 耐高温 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4