| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |||
| 1.32 g/cc | 0.0477 lb/in³ | DAM; ISO 1183 | |||
| Water Absorption | 6.4 % @Thickness 2.00 mm |
6.4 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Moisture Absorption | 2.00 % @Thickness 2.00 mm |
2.00 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Viscosity | 57704 cP @Shear Rate 5000 1/s, Temperature 305 °C |
57704 cP @Shear Rate 5000 1/s, Temperature 581 °F |
ISO 11403-1 -2 | ||
| 68380 cP @Shear Rate 5000 1/s, Temperature 295 °C |
68380 cP @Shear Rate 5000 1/s, Temperature 563 °F |
ISO 11403-1 -2 | |||
| 82058 cP @Shear Rate 5000 1/s, Temperature 285 °C |
82058 cP @Shear Rate 5000 1/s, Temperature 545 °F |
ISO 11403-1 -2 | |||
| 164300 cP @Shear Rate 500 1/s, Temperature 305 °C |
164300 cP @Shear Rate 500 1/s, Temperature 581 °F |
ISO 11403-1 -2 | |||
| 204000 cP @Shear Rate 500 1/s, Temperature 295 °C |
204000 cP @Shear Rate 500 1/s, Temperature 563 °F |
ISO 11403-1 -2 | |||
| 254600 cP @Shear Rate 500 1/s, Temperature 285 °C |
254600 cP @Shear Rate 500 1/s, Temperature 545 °F |
ISO 11403-1 -2 | |||
| Viscosity Test | 140 cm³/g | 140 cm³/g | DAM; ISO 307 1157 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 260 MPa | 37700 psi | DAM; H 961/30; ISO 2039-1 | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | 50%RH; ISO 527-1/-2 | ||
| 180 MPa | 26100 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 3.0 % | 3.0 % | DAM; ISO 527-1/-2 | ||
| 7.0 % | 7.0 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 6.10 GPa | 885 ksi | 50%RH; ISO 527-1/-2 | ||
| 8.40 GPa | 1220 ksi | DAM; ISO 527-1/-2 | |||
| 3.174 GPa @Temperature 170 °C |
460.4 ksi @Temperature 338 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 3.986 GPa @Temperature 110 °C |
578.1 ksi @Temperature 230 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 7.555 GPa @Temperature 30.0 °C |
1096 ksi @Temperature 86.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 7.701 GPa @Temperature -20.0 °C |
1117 ksi @Temperature -4.00 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 8.133 GPa @Temperature -70.0 °C |
1180 ksi @Temperature -94.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 8.485 GPa @Temperature -100 °C |
1231 ksi @Temperature -148 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | DAM; ISO 179/1eU | ||
| 8.00 J/cm² | 38.1 ft-lb/in² | 50%RH; ISO 179/1eU | |||
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |||
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | DAM; ISO 179/1eA | ||
| 1.10 J/cm² | 5.23 ft-lb/in² | 50%RH; ISO 179/1eA | |||
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DAM; IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | 50%RH; IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 100 Hz |
3.6 @Frequency 100 Hz |
DAM; IEC 60250 | ||
| Dissipation Factor | 0.0070 @Frequency 100 Hz |
0.0070 @Frequency 100 Hz |
DAM; IEC 60250 | ||
| Comparative Tracking Index | 400 V | 400 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 33.0 µm/m-°C | 18.3 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 112 µm/m-°C | 62.2 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| Specific Heat Capacity | 2.09 J/g-°C @Thickness 1.50 mm |
0.500 BTU/lb-°F @Thickness 0.0591 in |
|||
| Thermal Conductivity | 0.210 W/m-K | 1.46 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 262 °C | 504 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | DAM; ISO 75-1/-2 | ||
| Vicat Softening Point | 257 °C | 495 °F | DAM; 50°C/h 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | DAM; 10°C/min; ISO 11357-1/-2 | ||
| Flame Spread | 26 mm/min @Thickness 1.00 mm |
1.0 in/min @Thickness 0.0394 in |
ISO 3795 (FMVSS 302) | ||
| De |
|||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Odour | class 3.5 | VDA 270 | |||
| Part Marking Code | >PA66-GF25< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA66-GF25 | ||||
| Special characteristics | Heat stabilised or stable to heat | ||||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。
上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！
可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：
联系人：邓小姐
联系电话：13917657923
联系QQ:996152797
联系邮箱：996152797@qq.com