  4. 热稳定高强度PA66/美国杜邦/70G35HSL NC010

热稳定高强度PA66/美国杜邦/70G35HSL NC010

热稳定高强度PA66/美国杜邦/70G35HSL NC010
 参考图片：

颗粒图片：

包装图片：

成品图片：
f99c6df6dda12fe1_1

 

 

 
Physical Properties Metric English Comments
Density  1.24 g/cc 0.0448 lb/in³  
  1.41 g/cc 0.0509 lb/in³ DAM; ISO 1183
Water Absorption  5.5 %
@Thickness 2.00 mm		 5.5 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  1.70 %
@Thickness 2.00 mm		 1.70 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Viscosity  69000 cP
@Shear Rate 5000 1/s,
Temperature 305 °C		 69000 cP
@Shear Rate 5000 1/s,
Temperature 581 °F		 ISO 11403-1 -2
  86000 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		 86000 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		 ISO 11403-1 -2
  137000 cP
@Shear Rate 5000 1/s,
Temperature 275 °C		 137000 cP
@Shear Rate 5000 1/s,
Temperature 527 °F		 ISO 11403-1 -2
  196000 cP
@Shear Rate 500 1/s,
Temperature 305 °C		 196000 cP
@Shear Rate 500 1/s,
Temperature 581 °F		 ISO 11403-1 -2
  248000 cP
@Shear Rate 500 1/s,
Temperature 295 °C		 248000 cP
@Shear Rate 500 1/s,
Temperature 563 °F		 ISO 11403-1 -2
  404000 cP
@Shear Rate 500 1/s,
Temperature 275 °C		 404000 cP
@Shear Rate 500 1/s,
Temperature 527 °F		 ISO 11403-1 -2
Viscosity Test  145 cm³/g 145 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.011 cm/cm 0.011 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  89 89 50%RH; ISO 2039-2
  105 105 DAM; ISO 2039-2
Hardness, Rockwell R  117 117 50%RH; ISO 2039-2
  125 125 DAM; ISO 2039-2
Tensile Strength at Break  145 MPa 21000 psi 50%RH; ISO 527-1/-2
  210 MPa 30500 psi DAM; ISO 527-1/-2
Tensile Stress   7.61 MPa
@Strain 0.150 %,
Temperature 90.0 °C		 1100 psi
@Strain 0.150 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  10.92 MPa
@Strain 0.250 %,
Temperature 150 °C		 1584 psi
@Strain 0.250 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  11.43 MPa
@Strain 0.280 %,
Temperature 150 °C		 1658 psi
@Strain 0.280 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  15.04 MPa
@Strain 0.270 %,
Temperature 90.0 °C		 2181 psi
@Strain 0.270 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  19.29 MPa
@Strain 0.300 %,
Temperature 23.0 °C		 2798 psi
@Strain 0.300 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  20.06 MPa
@Strain 0.330 %,
Temperature 40.0 °C		 2909 psi
@Strain 0.330 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  39.28 MPa
@Strain 1.31 %,
Temperature 150 °C		 5697 psi
@Strain 1.31 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  47.25 MPa
@Strain 1.20 %,
Temperature 90.0 °C		 6853 psi
@Strain 1.20 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  48.84 MPa
@Strain 1.48 %,
Temperature 150 °C		 7084 psi
@Strain 1.48 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  51.17 MPa
@Strain 2.07 %,
Temperature 150 °C		 7422 psi
@Strain 2.07 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  53.63 MPa
@Strain 0.490 %,
Temperature -20.0 °C		 7778 psi
@Strain 0.490 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  55.7 MPa
@Strain 0.610 %,
Temperature 0.000 °C		 8080 psi
@Strain 0.610 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  57.58 MPa
@Strain 0.590 %,
Temperature 40.0 °C		 8351 psi
@Strain 0.590 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  59.43 MPa
@Strain 2.86 %,
Temperature 150 °C		 8620 psi
@Strain 2.86 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  64.21 MPa
@Strain 1.48 %,
Temperature 90.0 °C		 9313 psi
@Strain 1.48 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  64.53 MPa
@Strain 2.39 %,
Temperature 150 °C		 9359 psi
@Strain 2.39 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  65.31 MPa
@Strain 1.97 %,
Temperature 90.0 °C		 9472 psi
@Strain 1.97 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  65.53 MPa
@Strain 1.32 %,
Temperature 40.0 °C		 9504 psi
@Strain 1.32 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  67.63 MPa
@Strain 0.640 %,
Temperature -20.0 °C		 9809 psi
@Strain 0.640 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  69.45 MPa
@Strain 0.670 %,
Temperature 0.000 °C		 10070 psi
@Strain 0.670 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  69.61 MPa
@Strain 1.25 %,
Temperature 23.0 °C		 10100 psi
@Strain 1.25 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  75.35 MPa
@Strain 3.32 %,
Temperature 150 °C		 10930 psi
@Strain 3.32 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  77.54 MPa
@Strain 2.78 %,
Temperature 90.0 °C		 11250 psi
@Strain 2.78 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  80.8 MPa
@Strain 0.822 %,
Temperature 23.0 °C		 11700 psi
@Strain 0.822 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  85.96 MPa
@Strain 2.33 %,
Temperature 90.0 °C		 12470 psi
@Strain 2.33 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  86.61 MPa
@Strain 2.02 %,
Temperature 40.0 °C		 12560 psi
@Strain 2.02 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  89.5 MPa
@Strain 6.72 %,
Temperature 150 °C		 13000 psi
@Strain 6.72 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  95.98 MPa
@Strain 1.99 %,
Temperature 23.0 °C		 13920 psi
@Strain 1.99 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  101.06 MPa
@Strain 3.14 %,
Temperature 90.0 °C		 14658 psi
@Strain 3.14 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  101.42 MPa
@Strain 2.71 %,
Temperature 40.0 °C		 14710 psi
@Strain 2.71 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  109.93 MPa
@Strain 1.40 %,
Temperature 0.000 °C		 15944 psi
@Strain 1.40 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  114.76 MPa
@Strain 2.74 %,
Temperature 23.0 °C		 16645 psi
@Strain 2.74 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  115.13 MPa
@Strain 1.31 %,
Temperature 40.0 °C		 16698 psi
@Strain 1.31 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  118.45 MPa
@Strain 1.19 %,
Temperature 0.000 °C		 17180 psi
@Strain 1.19 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  134.55 MPa
@Strain 1.91 %,
Temperature 0.000 °C		 19515 psi
@Strain 1.91 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  136.97 MPa
@Strain 1.44 %,
Temperature -20.0 °C		 19866 psi
@Strain 1.44 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  138.77 MPa
@Strain 1.72 %,
Temperature 40.0 °C		 20127 psi
@Strain 1.72 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  146.75 MPa
@Strain 1.63 %,
Temperature 23.0 °C		 21284 psi
@Strain 1.63 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  154.33 MPa
@Strain 2.44 %,
Temperature 0.000 °C		 22384 psi
@Strain 2.44 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  157.07 MPa
@Strain 1.70 %,
Temperature 0.000 °C		 22781 psi
@Strain 1.70 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  160.1 MPa
@Strain 2.23 %,
Temperature 40.0 °C		 23220 psi
@Strain 2.23 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  167.61 MPa
@Strain 1.93 %,
Temperature -20.0 °C		 24310 psi
@Strain 1.93 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  173.95 MPa
@Strain 2.08 %,
Temperature 23.0 °C		 25229 psi
@Strain 2.08 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  174.6 MPa
@Strain 1.84 %,
Temperature -20.0 °C		 25320 psi
@Strain 1.84 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  183.67 MPa
@Strain 2.11 %,
Temperature 0.000 °C		 26639 psi
@Strain 2.11 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  190.98 MPa
@Strain 2.43 %,
Temperature -20.0 °C		 27699 psi
@Strain 2.43 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  197.12 MPa
@Strain 2.61 %,
Temperature 23.0 °C		 28590 psi
@Strain 2.61 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  203.2 MPa
@Strain 2.28 %,
Temperature -20.0 °C		 29470 psi
@Strain 2.28 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  237.16 MPa
@Strain 2.92 %,
Temperature -20.0 °C		 34397 psi
@Strain 2.92 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
Elongation at Break  3.2 % 3.2 % DAM; ISO 527-1/-2
  4.6 % 4.6 % 50%RH; ISO 527-1/-2
Tensile Modulus  8.30 GPa 1200 ksi 50%RH; ISO 527-1/-2
  11.2 GPa 1620 ksi DAM; ISO 527-1/-2
  3.707 GPa
@Temperature 150 °C		 537.7 ksi
@Temperature 302 °F		 50%RH; ISO 11403-1 -2
  4.208 GPa
@Temperature 150 °C		 610.3 ksi
@Temperature 302 °F		 DAM; ISO 11403-1 -2
  5.609 GPa
@Temperature 60.0 °C		 813.5 ksi
@Temperature 140 °F		 50%RH; ISO 11403-1 -2
  7.533 GPa
@Temperature 60.0 °C		 1093 ksi
@Temperature 140 °F		 DAM; ISO 11403-1 -2
  10.749 GPa
@Temperature -20.0 °C		 1559.0 ksi
@Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  10.893 GPa
@Temperature -20.0 °C		 1579.9 ksi
@Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
Shear Modulus   0.726 GPa
@Temperature 150 °C		 105 ksi
@Temperature 302 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.7911 GPa
@Temperature 110 °C		 114.7 ksi
@Temperature 230 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.005 GPa
@Temperature 60.0 °C		 145.8 ksi
@Temperature 140 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.9484 GPa
@Temperature 10.0 °C		 282.60 ksi
@Temperature 50.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  2.0978 GPa
@Temperature -20.0 °C		 304.26 ksi
@Temperature -4.00 °F		 DAM; Dynamic; ISO 11403-1 -2
  2.1781 GPa
@Temperature -50.0 °C		 315.91 ksi
@Temperature -58.0 °F		 DAM; Dynamic; ISO 11403-1 -2
Shear Strength  0.0980 MPa
@Shear Rate 500 1/s,
Temperature 305 °C		 14.2 psi
@Shear Rate 500 1/s,
Temperature 581 °F		 ISO 11403-1 -2
  0.124 MPa
@Shear Rate 500 1/s,
Temperature 295 °C		 18.0 psi
@Shear Rate 500 1/s,
Temperature 563 °F		 ISO 11403-1 -2
  0.202 MPa
@Shear Rate 500 1/s,
Temperature 275 °C		 29.3 psi
@Shear Rate 500 1/s,
Temperature 527 °F		 ISO 11403-1 -2
Secant Modulus   2.58 GPa
@Strain 4.49 %,
Temperature 40.0 °C		 373 ksi
@Strain 4.49 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  3.03 GPa
@Strain 4.35 %,
Temperature 23.0 °C		 439 ksi
@Strain 4.35 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.36 GPa
@Strain 3.23 %,
Temperature 40.0 °C		 487 ksi
@Strain 3.23 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  3.85 GPa
@Strain 3.19 %,
Temperature 23.0 °C		 559 ksi
@Strain 3.19 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.11 GPa
@Strain 2.24 %,
Temperature 40.0 °C		 596 ksi
@Strain 2.24 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  4.53 GPa
@Strain 3.94 %,
Temperature 0.000 °C		 658 ksi
@Strain 3.94 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.60 GPa
@Strain 2.25 %,
Temperature 23.0 °C		 667 ksi
@Strain 2.25 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.96 GPa
@Strain 1.32 %,
Temperature 40.0 °C		 720 ksi
@Strain 1.32 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  5.5688 GPa
@Strain 1.25 %,
Temperature 23.0 °C		 807.70 ksi
@Strain 1.25 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5.86 GPa
@Strain 2.83 %,
Temperature 0.000 °C		 850 ksi
@Strain 2.83 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.89 GPa
@Strain 3.75 %,
Temperature -20.0 °C		 854 ksi
@Strain 3.75 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  6.08 GPa
@Strain 0.330 %,
Temperature 40.0 °C		 882 ksi
@Strain 0.330 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  6.43 GPa
@Strain 0.300 %,
Temperature 23.0 °C		 933 ksi
@Strain 0.300 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  6.54 GPa
@Strain 2.63 %,
Temperature 40.0 °C		 948 ksi
@Strain 2.63 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  6.80 GPa
@Strain 2.08 %,
Temperature 0.000 °C		 986 ksi
@Strain 2.08 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  6.92 GPa
@Strain 3.04 %,
Temperature 23.0 °C		 1000 ksi
@Strain 3.04 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  7.1739 GPa
@Strain 3.18 %,
Temperature 0.000 °C		 1040.5 ksi
@Strain 3.18 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  7.37 GPa
@Strain 2.77 %,
Temperature -20.0 °C		 1070 ksi
@Strain 2.77 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  7.45 GPa
@Strain 3.36 %,
Temperature -20.0 °C		 1080 ksi
@Strain 3.36 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  7.77 GPa
@Strain 1.88 %,
Temperature 40.0 °C		 1130 ksi
@Strain 1.88 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  7.85 GPa
@Strain 1.40 %,
Temperature 0.000 °C		 1140 ksi
@Strain 1.40 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  8.11 GPa
@Strain 2.24 %,
Temperature 23.0 °C		 1180 ksi
@Strain 2.24 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  8.27 GPa
@Strain 2.42 %,
Temperature 0.000 °C		 1200 ksi
@Strain 2.42 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  8.3881 GPa
@Strain 2.10 %,
Temperature -20.0 °C		 1216.6 ksi
@Strain 2.10 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  8.71 GPa
@Strain 2.43 %,
Temperature -20.0 °C		 1260 ksi
@Strain 2.43 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  8.79 GPa
@Strain 1.31 %,
Temperature 40.0 °C		 1270 ksi
@Strain 1.31 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  9.00 GPa
@Strain 1.63 %,
Temperature 23.0 °C		 1310 ksi
@Strain 1.63 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  9.08 GPa
@Strain 1.83 %,
Temperature 0.000 °C		 1320 ksi
@Strain 1.83 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  9.13 GPa
@Strain 0.610 %,
Temperature 0.000 °C		 1320 ksi
@Strain 0.610 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  9.49 GPa
@Strain 1.84 %,
Temperature -20.0 °C		 1380 ksi
@Strain 1.84 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  9.51 GPa
@Strain 1.44 %,
Temperature -20.0 °C		 1380 ksi
@Strain 1.44 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  9.76 GPa
@Strain 0.590 %,
Temperature 40.0 °C		 1420 ksi
@Strain 0.590 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  9.83 GPa
@Strain 0.822 %,
Temperature 23.0 °C		 1430 ksi
@Strain 0.822 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  9.95 GPa
@Strain 1.19 %,
Temperature 0.000 °C		 1440 ksi
@Strain 1.19 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  10.4 GPa
@Strain 0.670 %,
Temperature 0.000 °C		 1500 ksi
@Strain 0.670 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  10.6 GPa
@Strain 0.640 %,
Temperature -20.0 °C		 1530 ksi
@Strain 0.640 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  10.9 GPa
@Strain 0.490 %,
Temperature -20.0 °C		 1590 ksi
@Strain 0.490 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  12.0 kJ/m² 5.71 ft-lb/in² DAM; ISO 180/1A
  15.0 kJ/m² 7.14 ft-lb/in² 50%RH; ISO 180/1A
  10.0 kJ/m²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
  10.0 kJ/m²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
Charpy Impact Unnotched  9.00 J/cm² 42.8 ft-lb/in² DAM; ISO 179/1eU
  10.0 J/cm² 47.6 ft-lb/in² 50%RH; ISO 179/1eU
  7.50 J/cm²
@Temperature -30.0 °C		 35.7 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
  8.00 J/cm²
@Temperature -30.0 °C		 38.1 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
Charpy Impact, Notched  1.50 J/cm² 7.14 ft-lb/in² DAM; ISO 179/1eA
  1.80 J/cm² 8.57 ft-lb/in² 50%RH; ISO 179/1eA
  1.00 J/cm²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  1.00 J/cm²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
Puncture Energy  6.00 J 4.43 ft-lb DAM; ISO 6603-2
Tensile Creep Modulus, 1 hour  8400 MPa
@Time 3600 sec		 1.22e+6 psi
@Time 1.00 hour		 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours  6000 MPa
@Time 3.60e+6 sec		 870000 psi
@Time 1000 hour		 50%RH; ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+11 ohm-cm 1.00e+11 ohm-cm 50%RH; IEC 60093
  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm DAM; IEC 60093
Surface Resistance  1.00e+13 ohm 1.00e+13 ohm 50%RH; IEC 60093
Dielectric Strength  31.0 kV/mm 787 kV/in 50%RH; IEC 60243-1
  36.0 kV/mm 914 kV/in DAM; IEC 60243-1
Comparative Tracking Index  400 V 400 V DAM; IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  20.0 µm/m-°C 11.1 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  100 µm/m-°C 55.6 µin/in-°F DAM; ISO 11359-1/-2
Specific Heat Capacity  2.13 J/g-°C 0.509 BTU/lb-°F  
Thermal Conductivity  0.240 W/m-K 1.67 BTU-in/hr-ft²-°F of melt
Melting Point  262 °C 504 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  261 °C 502 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  252 °C 486 °F DAM; ISO 75-1/-2
Vicat Softening Point  255 °C 491 °F DAM; 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  80.0 °C 176 °F DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 0.700 mm		 HB
@Thickness 0.0276 in		 DAM; IEC 60695-11-10
Oxygen Index  24 % 24 % DAM; ISO 4589-1/-2
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >PA66-GF35< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA66-GF35  
Special characteristics Heat stabilised or stable to heat  
UL recognition UL DAM

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39799.html

免责声明: 本文 热稳定高强度PA66/美国杜邦/70G35HSL NC010 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4