| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | DAM; ISO 1183 | ||
| Viscosity | 33500 cP @Shear Rate 5000 1/s, Temperature 300 °C |
33500 cP @Shear Rate 5000 1/s, Temperature 572 °F |
ISO 11403-1 -2 | ||
| 40900 cP @Shear Rate 5000 1/s, Temperature 290 °C |
40900 cP @Shear Rate 5000 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 46800 cP @Shear Rate 5000 1/s, Temperature 280 °C |
46800 cP @Shear Rate 5000 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| 74300 cP @Shear Rate 500 1/s, Temperature 300 °C |
74300 cP @Shear Rate 500 1/s, Temperature 572 °F |
ISO 11403-1 -2 | |||
| 90200 cP @Shear Rate 500 1/s, Temperature 290 °C |
90200 cP @Shear Rate 500 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 110900 cP @Shear Rate 500 1/s, Temperature 280 °C |
110900 cP @Shear Rate 500 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| Viscosity Test | 83 cm³/g | 83 cm³/g | DAM; sulphuric acid 96%; ISO 307 1157 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 2577 | ||
| 0.0020 cm/cm @Thickness 3.20 mm |
0.0020 in/in @Thickness 0.126 in |
DAM | |||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | DAM; ISO 294-4 2577 | ||
| 0.010 cm/cm @Thickness 3.20 mm |
0.010 in/in @Thickness 0.126 in |
DAM; ASTM D149 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | 50%RH; ISO 527-1/-2 | ||
| 168 MPa | 24400 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 3.0 % | 3.0 % | DAM; ISO 527-1/-2 | ||
| 3.2 % | 3.2 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 7.90 GPa | 1150 ksi | 50%RH; ISO 527-1/-2 | ||
| 9.50 GPa | 1380 ksi | DAM; ISO 527-1/-2 | |||
| Flexural Modulus | 8.20 GPa | 1190 ksi | DAM; ISO 178 | ||
| Shear Modulus | 0.5491 GPa @Temperature 150 °C |
79.64 ksi @Temperature 302 °F |
DAM; Dynamic; ISO 11403-1 -2 | ||
| 0.7167 GPa @Temperature 110 °C |
104.0 ksi @Temperature 230 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 1.0778 GPa @Temperature 60.0 °C |
156.32 ksi @Temperature 140 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 1.7138 GPa @Temperature 10.0 °C |
248.57 ksi @Temperature 50.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 1.7428 GPa @Temperature -20.0 °C |
252.78 ksi @Temperature -4.00 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 1.8178 GPa @Temperature -50.0 °C |
263.65 ksi @Temperature -58.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| Shear Strength | 0.009685 MPa @Shear Rate 50.0 1/s, Temperature 300 °C |
1.405 psi @Shear Rate 50.0 1/s, Temperature 572 °F |
ISO 11403-1 -2 | ||
| 0.01373 MPa @Shear Rate 50.0 1/s, Temperature 290 °C |
1.991 psi @Shear Rate 50.0 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 0.01426 MPa @Shear Rate 50.0 1/s, Temperature 280 °C |
2.068 psi @Shear Rate 50.0 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| 0.03715 MPa @Shear Rate 500 1/s, Temperature 300 °C |
5.388 psi @Shear Rate 500 1/s, Temperature 572 °F |
ISO 11403-1 -2 | |||
| 0.0451 MPa @Shear Rate 500 1/s, Temperature 290 °C |
6.54 psi @Shear Rate 500 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 0.05545 MPa @Shear Rate 500 1/s, Temperature 280 °C |
8.042 psi @Shear Rate 500 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| 0.1675 MPa @Shear Rate 5000 1/s, Temperature 300 °C |
24.29 psi @Shear Rate 5000 1/s, Temperature 572 °F |
ISO 11403-1 -2 | |||
| 0.2045 MPa @Shear Rate 5000 1/s, Temperature 290 °C |
29.66 psi @Shear Rate 5000 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 0.234 MPa @Shear Rate 5000 1/s, Temperature 280 °C |
33.9 psi @Shear Rate 5000 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | DAM; ISO 180/1A | ||
| 11.0 kJ/m² @Temperature -40.0 °C |
5.23 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | DAM; ISO 179/1eA | ||
| 1.20 J/cm² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V | 600 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| 14.0 µm/m-°C @Temperature 55.0 - 160 °C |
7.78 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |||
| 26.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
14.4 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 113 µm/m-°C | 62.8 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| 83.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
46.1 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |||
| 158 µm/m-°C @Temperature 55.0 - 160 °C |
87.8 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |||
| Melting Point | 218 °C | 424 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 65.0 °C | 149 °F | DAM; 10°C/min; ISO 11357-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.700 mm |
HB @Thickness 0.0276 in |
DAM; IEC 60695-11-10 | ||
| De |
|||||
| Part Marking Code | >PA612-GF33< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA612-GF33 | ||||
| PA612-GF33 | ISO 1043 | ||||
| UL recognition | UL | DAM | |||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。