耐高温 PA66/美国杜邦/80G33HS1L NC010

耐高温 热稳定 PA66/美国杜邦/80G33HS1L NC010
 参考图片：

颗粒图片：

包装图片：

成品图片：
images (5)
 

 

 

Physical Properties Metric English Comments
Density  1.12 g/cc 0.0405 lb/in³  
  1.33 g/cc 0.0480 lb/in³ DAM; ISO 1183
Water Absorption  4.5 %
@Thickness 2.00 mm		 4.5 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  1.50 %
@Thickness 2.00 mm		 1.50 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Water Absorption at Saturation  0.85 % 0.85 % DAM; Immersion 24h; ASTM D570
Viscosity   69805 cP
@Shear Rate 5000 1/s,
Temperature 305 °C		 69805 cP
@Shear Rate 5000 1/s,
Temperature 581 °F		 ISO 11403-1 -2
  88510 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		 88510 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		 ISO 11403-1 -2
  115100 cP
@Shear Rate 5000 1/s,
Temperature 285 °C		 115100 cP
@Shear Rate 5000 1/s,
Temperature 545 °F		 ISO 11403-1 -2
  241800 cP
@Shear Rate 500 1/s,
Temperature 305 °C		 241800 cP
@Shear Rate 500 1/s,
Temperature 581 °F		 ISO 11403-1 -2
  308700 cP
@Shear Rate 500 1/s,
Temperature 295 °C		 308700 cP
@Shear Rate 500 1/s,
Temperature 563 °F		 ISO 11403-1 -2
  403200 cP
@Shear Rate 500 1/s,
Temperature 285 °C		 403200 cP
@Shear Rate 500 1/s,
Temperature 545 °F		 ISO 11403-1 -2
Viscosity Test  160 cm³/g 160 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0070 cm/cm 0.0070 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  70 70 DAM; ISO 2039-2
Hardness, Rockwell R  110 110 DAM; ISO 2039-2
Tensile Strength at Break  108 MPa 15700 psi 50%RH; ISO 527-1/-2
  146 MPa 21200 psi DAM; ISO 527-1/-2
Tensile Stress   8.47 MPa
@Strain 0.230 %,
Temperature 150 °C		 1230 psi
@Strain 0.230 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  10.7 MPa
@Strain 0.240 %,
Temperature 90.0 °C		 1550 psi
@Strain 0.240 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  11.24 MPa
@Strain 0.240 %,
Temperature 90.0 °C		 1630 psi
@Strain 0.240 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  13.42 MPa
@Strain 0.420 %,
Temperature 150 °C		 1946 psi
@Strain 0.420 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  19.37 MPa
@Strain 0.330 %,
Temperature 40.0 °C		 2809 psi
@Strain 0.330 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  26.06 MPa
@Strain 0.820 %,
Temperature 150 °C		 3780 psi
@Strain 0.820 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  30.98 MPa
@Strain 1.24 %,
Temperature 150 °C		 4493 psi
@Strain 1.24 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  31.49 MPa
@Strain 0.830 %,
Temperature 90.0 °C		 4567 psi
@Strain 0.830 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  34.96 MPa
@Strain 0.310 %,
Temperature -40.0 °C		 5071 psi
@Strain 0.310 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  36.33 MPa
@Strain 0.890 %,
Temperature 90.0 °C		 5269 psi
@Strain 0.890 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  41.33 MPa
@Strain 0.590 %,
Temperature 23.0 °C		 5994 psi
@Strain 0.590 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  44.4 MPa
@Strain 2.51 %,
Temperature 150 °C		 6440 psi
@Strain 2.51 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  44.82 MPa
@Strain 0.510 %,
Temperature 40.0 °C		 6501 psi
@Strain 0.510 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  45.52 MPa
@Strain 1.99 %,
Temperature 150 °C		 6602 psi
@Strain 1.99 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  51.14 MPa
@Strain 1.03 %,
Temperature 40.0 °C		 7417 psi
@Strain 1.03 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  53.18 MPa
@Strain 4.05 %,
Temperature 150 °C		 7713 psi
@Strain 4.05 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  53.24 MPa
@Strain 1.88 %,
Temperature 90.0 °C		 7722 psi
@Strain 1.88 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  58.28 MPa
@Strain 3.57 %,
Temperature 150 °C		 8453 psi
@Strain 3.57 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  59.6 MPa
@Strain 0.710 %,
Temperature 0.000 °C		 8640 psi
@Strain 0.710 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  62.58 MPa
@Strain 1.99 %,
Temperature 90.0 °C		 9076 psi
@Strain 1.99 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  67.95 MPa
@Strain 3.35 %,
Temperature 90.0 °C		 9855 psi
@Strain 3.35 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  69.02 MPa
@Strain 0.760 %,
Temperature 23.0 °C		 10010 psi
@Strain 0.760 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  69.98 MPa
@Strain 0.740 %,
Temperature -20.0 °C		 10150 psi
@Strain 0.740 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  76.42 MPa
@Strain 1.31 %,
Temperature 23.0 °C		 11080 psi
@Strain 1.31 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  79.23 MPa
@Strain 2.10 %,
Temperature 40.0 °C		 11490 psi
@Strain 2.10 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  81.91 MPa
@Strain 3.42 %,
Temperature 90.0 °C		 11880 psi
@Strain 3.42 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  88.29 MPa
@Strain 0.870 %,
Temperature -40.0 °C		 12810 psi
@Strain 0.870 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  90.52 MPa
@Strain 1.19 %,
Temperature 40.0 °C		 13130 psi
@Strain 1.19 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  90.65 MPa
@Strain 0.980 %,
Temperature 0.000 °C		 13150 psi
@Strain 0.980 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  96.81 MPa
@Strain 3.55 %,
Temperature 40.0 °C		 14040 psi
@Strain 3.55 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  100.09 MPa
@Strain 1.07 %,
Temperature -40.0 °C		 14517 psi
@Strain 1.07 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  100.58 MPa
@Strain 1.35 %,
Temperature 0.000 °C		 14588 psi
@Strain 1.35 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  104.57 MPa
@Strain 2.27 %,
Temperature 23.0 °C		 15167 psi
@Strain 2.27 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  105.95 MPa
@Strain 1.16 %,
Temperature -20.0 °C		 15367 psi
@Strain 1.16 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  114.59 MPa
@Strain 1.47 %,
Temperature 23.0 °C		 16620 psi
@Strain 1.47 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  115.64 MPa
@Strain 1.36 %,
Temperature -20.0 °C		 16772 psi
@Strain 1.36 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  121.49 MPa
@Strain 3.63 %,
Temperature 23.0 °C		 17621 psi
@Strain 3.63 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  127.79 MPa
@Strain 2.22 %,
Temperature 40.0 °C		 18534 psi
@Strain 2.22 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  134.54 MPa
@Strain 2.17 %,
Temperature 0.000 °C		 19513 psi
@Strain 2.17 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  140.54 MPa
@Strain 1.57 %,
Temperature -40.0 °C		 20384 psi
@Strain 1.57 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  142.15 MPa
@Strain 1.79 %,
Temperature 0.000 °C		 20617 psi
@Strain 1.79 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  143.3 MPa
@Strain 4.06 %,
Temperature 40.0 °C		 20780 psi
@Strain 4.06 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  151.92 MPa
@Strain 2.49 %,
Temperature 23.0 °C		 22034 psi
@Strain 2.49 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  153.48 MPa
@Strain 1.89 %,
Temperature -20.0 °C		 22260 psi
@Strain 1.89 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  154.85 MPa
@Strain 2.14 %,
Temperature -20.0 °C		 22459 psi
@Strain 2.14 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  157.32 MPa
@Strain 3.39 %,
Temperature 0.000 °C		 22817 psi
@Strain 3.39 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  158.08 MPa
@Strain 1.86 %,
Temperature -40.0 °C		 22928 psi
@Strain 1.86 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  181.01 MPa
@Strain 3.02 %,
Temperature 0.000 °C		 26253 psi
@Strain 3.02 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  185.08 MPa
@Strain 3.21 %,
Temperature -20.0 °C		 26844 psi
@Strain 3.21 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  186.91 MPa
@Strain 2.46 %,
Temperature -40.0 °C		 27109 psi
@Strain 2.46 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  193.42 MPa
@Strain 2.84 %,
Temperature -20.0 °C		 28053 psi
@Strain 2.84 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  209.81 MPa
@Strain 2.88 %,
Temperature -40.0 °C		 30430 psi
@Strain 2.88 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Elongation at Break  3.7 % 3.7 % DAM; ISO 527-1/-2
  7.0 % 7.0 % 50%RH; ISO 527-1/-2
Tensile Modulus  6.20 GPa 899 ksi 50%RH; ISO 527-1/-2
  8.90 GPa 1290 ksi DAM; ISO 527-1/-2
  1.83 GPa
@Temperature 225 °C		 265 ksi
@Temperature 437 °F		 DAM; Dynamic; ISO 11403-1 -2
  3.18 GPa
@Temperature 145 °C		 461 ksi
@Temperature 293 °F		 DAM; Dynamic; ISO 11403-1 -2
  3.578 GPa
@Temperature 120 °C		 518.9 ksi
@Temperature 248 °F		 50%RH; ISO 11403-1 -2
  4.215 GPa
@Temperature 120 °C		 611.3 ksi
@Temperature 248 °F		 DAM; ISO 11403-1 -2
  4.57 GPa
@Temperature 85.0 °C		 662 ksi
@Temperature 185 °F		 DAM; Dynamic; ISO 11403-1 -2
  5.636 GPa
@Temperature 40.0 °C		 817.4 ksi
@Temperature 104 °F		 50%RH; ISO 11403-1 -2
  7.4963 GPa
@Temperature 55.0 °C		 1087.2 ksi
@Temperature 131 °F		 DAM; Dynamic; ISO 11403-1 -2
  8.468 GPa
@Temperature 15.0 °C		 1228 ksi
@Temperature 59.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  8.484 GPa
@Temperature -10.0 °C		 1231 ksi
@Temperature 14.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  8.70 GPa
@Temperature 40.0 °C		 1260 ksi
@Temperature 104 °F		 DAM; ISO 11403-1 -2
  8.75 GPa
@Temperature -35.0 °C		 1270 ksi
@Temperature -31.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  9.26 GPa
@Temperature -50.0 °C		 1340 ksi
@Temperature -58.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  10.534 GPa
@Temperature -40.0 °C		 1527.8 ksi
@Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  10.72 GPa
@Temperature -40.0 °C		 1555 ksi
@Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Flexural Modulus  6.20 GPa 899 ksi 50%RH; ISO 178
  7.50 GPa 1090 ksi DAM; ISO 178
Shear Modulus   0.475 GPa
@Temperature 160 °C		 68.9 ksi
@Temperature 320 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.555 GPa
@Temperature 120 °C		 80.5 ksi
@Temperature 248 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.922 GPa
@Temperature 70.0 °C		 134 ksi
@Temperature 158 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.46 GPa
@Temperature 20.0 °C		 212 ksi
@Temperature 68.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.55 GPa
@Temperature -20.0 °C		 225 ksi
@Temperature -4.00 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.85 GPa
@Temperature -50.0 °C		 268 ksi
@Temperature -58.0 °F		 DAM; Dynamic; ISO 11403-1 -2
Secant Modulus   2.14 GPa
@Strain 4.78 %,
Temperature 40.0 °C		 311 ksi
@Strain 4.78 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  2.52 GPa
@Strain 4.91 %,
Temperature 23.0 °C		 366 ksi
@Strain 4.91 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.41 GPa
@Strain 2.53 %,
Temperature 40.0 °C		 495 ksi
@Strain 2.53 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  4.20 GPa
@Strain 2.66 %,
Temperature 23.0 °C		 609 ksi
@Strain 2.66 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.97 GPa
@Strain 1.03 %,
Temperature 40.0 °C		 720 ksi
@Strain 1.03 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  5.0777 GPa
@Strain 2.69 %,
Temperature 40.0 °C		 736.47 ksi
@Strain 2.69 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  5.13 GPa
@Strain 3.64 %,
Temperature 0.000 °C		 744 ksi
@Strain 3.64 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.41 GPa
@Strain 2.97 %,
Temperature 23.0 °C		 785 ksi
@Strain 2.97 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.71 GPa
@Strain 2.52 %,
Temperature 0.000 °C		 828 ksi
@Strain 2.52 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.83 GPa
@Strain 1.31 %,
Temperature 23.0 °C		 846 ksi
@Strain 1.31 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5.8697 GPa
@Strain 0.330 %,
Temperature 40.0 °C		 851.34 ksi
@Strain 0.330 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  6.30 GPa
@Strain 3.24 %,
Temperature -20.0 °C		 914 ksi
@Strain 3.24 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  6.55 GPa
@Strain 3.24 %,
Temperature -40.0 °C		 950 ksi
@Strain 3.24 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  6.73 GPa
@Strain 3.34 %,
Temperature -40.0 °C		 976 ksi
@Strain 3.34 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  6.79 GPa
@Strain 2.45 %,
Temperature -20.0 °C		 985 ksi
@Strain 2.45 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  7.01 GPa
@Strain 0.590 %,
Temperature 23.0 °C		 1020 ksi
@Strain 0.590 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  7.45 GPa
@Strain 1.35 %,
Temperature 0.000 °C		 1080 ksi
@Strain 1.35 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  7.61 GPa
@Strain 1.19 %,
Temperature 40.0 °C		 1100 ksi
@Strain 1.19 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  7.80 GPa
@Strain 1.47 %,
Temperature 23.0 °C		 1130 ksi
@Strain 1.47 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  7.94 GPa
@Strain 1.79 %,
Temperature 0.000 °C		 1150 ksi
@Strain 1.79 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  8.12 GPa
@Strain 1.89 %,
Temperature -20.0 °C		 1180 ksi
@Strain 1.89 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  8.39 GPa
@Strain 0.710 %,
Temperature 0.000 °C		 1220 ksi
@Strain 0.710 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  8.45 GPa
@Strain 1.84 %,
Temperature -40.0 °C		 1230 ksi
@Strain 1.84 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  8.50 GPa
@Strain 1.86 %,
Temperature -40.0 °C		 1230 ksi
@Strain 1.86 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  8.50 GPa
@Strain 1.36 %,
Temperature -20.0 °C		 1230 ksi
@Strain 1.36 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  8.79 GPa
@Strain 0.510 %,
Temperature 40.0 °C		 1270 ksi
@Strain 0.510 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  9.08 GPa
@Strain 0.760 %,
Temperature 23.0 °C		 1320 ksi
@Strain 0.760 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  9.13 GPa
@Strain 1.16 %,
Temperature -20.0 °C		 1320 ksi
@Strain 1.16 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  9.25 GPa
@Strain 0.980 %,
Temperature 0.000 °C		 1340 ksi
@Strain 0.980 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  9.35 GPa
@Strain 1.07 %,
Temperature -40.0 °C		 1360 ksi
@Strain 1.07 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  9.46 GPa
@Strain 0.740 %,
Temperature -20.0 °C		 1370 ksi
@Strain 0.740 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  10.1 GPa
@Strain 0.870 %,
Temperature -40.0 °C		 1470 ksi
@Strain 0.870 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  11.3 GPa
@Strain 0.310 %,
Temperature -40.0 °C		 1640 ksi
@Strain 0.310 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  21.0 kJ/m² 9.99 ft-lb/in² DAM; ISO 180/1A
  26.0 kJ/m² 12.4 ft-lb/in² 50%RH; ISO 180/1A
  15.0 kJ/m²
@Temperature -40.0 °C		 7.14 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
  15.0 kJ/m²
@Temperature -40.0 °C		 7.14 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 180/1A
  16.0 kJ/m²
@Temperature -30.0 °C		 7.61 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
  17.0 kJ/m²
@Temperature -30.0 °C		 8.09 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  80.0 kJ/m² 38.1 ft-lb/in² DAM; ISO 180/1U
  80.0 kJ/m² 38.1 ft-lb/in² 50%RH; ISO 180/1U
  75.0 kJ/m²
@Temperature -30.0 °C		 35.7 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1U
  80.0 kJ/m²
@Temperature -30.0 °C		 38.1 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1U
Charpy Impact Unnotched  9.70 J/cm² 46.2 ft-lb/in² DAM; ISO 179/1eU
  9.80 J/cm² 46.6 ft-lb/in² 50%RH; ISO 179/1eU
  10.0 J/cm²
@Temperature -30.0 °C		 47.6 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
  10.6 J/cm²
@Temperature -30.0 °C		 50.4 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
Charpy Impact, Notched  2.00 J/cm² 9.52 ft-lb/in² DAM; ISO 179/1eA
  2.80 J/cm² 13.3 ft-lb/in² 50%RH; ISO 179/1eA
  1.40 J/cm²
@Temperature -40.0 °C		 6.66 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
  1.70 J/cm²
@Temperature -30.0 °C		 8.09 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
  1.80 J/cm²
@Temperature -40.0 °C		 8.57 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 179/1eA
  1.80 J/cm²
@Temperature -30.0 °C		 8.57 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour  5300 MPa
@Time 3600 sec		 769000 psi
@Time 1.00 hour		 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours  4300 MPa
@Time 3.60e+6 sec		 624000 psi
@Time 1000 hour		 50%RH; ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+11 ohm-cm 1.00e+11 ohm-cm 50%RH; IEC 60093
  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm DAM; IEC 60093
Surface Resistance  1.00e+12 ohm 1.00e+12 ohm 50%RH; IEC 60093
Comparative Tracking Index  400 V 400 V DAM; IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  15.0 µm/m-°C 8.33 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  119 µm/m-°C 66.1 µin/in-°F DAM; ISO 11359-1/-2
  95.0 µm/m-°C
@Temperature -40.0 °C		 52.8 µin/in-°F
@Temperature -40.0 °F		 ISO 11403-1 -2
  95.0 µm/m-°C
@Temperature 23.0 °C		 52.8 µin/in-°F
@Temperature 73.4 °F		 ISO 11403-1 -2
Specific Heat Capacity  2.20 J/g-°C 0.526 BTU/lb-°F  
Thermal Conductivity  0.220 W/m-K 1.53 BTU-in/hr-ft²-°F of melt
Melting Point  262 °C 504 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  261 °C 502 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  246 °C 475 °F DAM; ISO 75-1/-2
Vicat Softening Point  245 °C 473 °F DAM; 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  75.0 °C 167 °F DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 DAM; IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Eff. thermal diffusivity 1.03E-07 m²/s  
Part Marking Code >PA66-IGF33< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA66-IGF33  
Special characteristics Heat stabilised or stable to heat  
UL recognition UL DAM

 

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39935.html

免责声明: 本文 耐高温 PA66/美国杜邦/80G33HS1L NC010 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4