| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | |||
| 1.32 g/cc | 0.0477 lb/in³ | DAM; ISO 1183 | |||
| Water Absorption at Saturation | 0.83 % | 0.83 % | DAM; Immersion 24h; ASTM D570 | ||
| Viscosity Test | 165 cm³/g | 165 cm³/g | DAM; ISO 307 1157 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 95.0 MPa | 13800 psi | 50%RH; ISO 527-1/-2 | ||
| 142 MPa | 20600 psi | DAM; ISO 527-1/-2 | |||
| Tensile Stress | 21.14 MPa @Strain 0.600 %, Temperature 90.0 °C |
3066 psi @Strain 0.600 %, Temperature 194 °F |
50%RH; ISO 11403-1 -2 | ||
| 24.19 MPa @Strain 0.680 %, Temperature 90.0 °C |
3508 psi @Strain 0.680 %, Temperature 194 °F |
DAM; ISO 11403-1 -2 | |||
| 27.72 MPa @Strain 0.630 %, Temperature 40.0 °C |
4020 psi @Strain 0.630 %, Temperature 104 °F |
50%RH; ISO 11403-1 -2 | |||
| 30.07 MPa @Strain 0.400 %, Temperature 40.0 °C |
4361 psi @Strain 0.400 %, Temperature 104 °F |
DAM; ISO 11403-1 -2 | |||
| 32.25 MPa @Strain 0.570 %, Temperature 23.0 °C |
4677 psi @Strain 0.570 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |||
| 52.19 MPa @Strain 2.24 %, Temperature 90.0 °C |
7570 psi @Strain 2.24 %, Temperature 194 °F |
50%RH; ISO 11403-1 -2 | |||
| 61.57 MPa @Strain 2.69 %, Temperature 90.0 °C |
8930 psi @Strain 2.69 %, Temperature 194 °F |
DAM; ISO 11403-1 -2 | |||
| 62.48 MPa @Strain 3.89 %, Temperature 90.0 °C |
9062 psi @Strain 3.89 %, Temperature 194 °F |
50%RH; ISO 11403-1 -2 | |||
| 70.96 MPa @Strain 2.40 %, Temperature 40.0 °C |
10290 psi @Strain 2.40 %, Temperature 104 °F |
50%RH; ISO 11403-1 -2 | |||
| 73.93 MPa @Strain 4.63 %, Temperature 90.0 °C |
10720 psi @Strain 4.63 %, Temperature 194 °F |
DAM; ISO 11403-1 -2 | |||
| 82.81 MPa @Strain 2.13 %, Temperature 23.0 °C |
12010 psi @Strain 2.13 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |||
| 85.05 MPa @Strain 4.18 %, Temperature 40.0 °C |
12340 psi @Strain 4.18 %, Temperature 104 °F |
50%RH; ISO 11403-1 -2 | |||
| 91.14 MPa @Strain 1.57 %, Temperature 40.0 °C |
13220 psi @Strain 1.57 %, Temperature 104 °F |
DAM; ISO 11403-1 -2 | |||
| 100.16 MPa @Strain 3.70 %, Temperature 23.0 °C |
14527 psi @Strain 3.70 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |||
| 115.12 MPa @Strain 2.74 %, Temperature 40.0 °C |
16697 psi @Strain 2.74 %, Temperature 104 °F |
DAM; ISO 11403-1 -2 | |||
| Elongation at Break | 4.0 % | 4.0 % | DAM; ISO 527-1/-2 | ||
| 5.0 % | 5.0 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 5.80 GPa | 841 ksi | 50%RH; ISO 527-1/-2 | ||
| 8.70 GPa | 1260 ksi | DAM; ISO 527-1/-2 | |||
| Flexural Modulus | 5.20 GPa | 754 ksi | 50%RH; ISO 178 | ||
| 7.40 GPa | 1070 ksi | DAM; ISO 178 | |||
| Secant Modulus | 1.81 GPa @Strain 4.77 %, Temperature 40.0 °C |
263 ksi @Strain 4.77 %, Temperature 104 °F |
50%RH; ISO 11403-1 -2 | ||
| 2.41 GPa @Strain 4.22 %, Temperature 23.0 °C |
350 ksi @Strain 4.22 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |||
| 2.96 GPa @Strain 2.40 %, Temperature 40.0 °C |
429 ksi @Strain 2.40 %, Temperature 104 °F |
50%RH; ISO 11403-1 -2 | |||
| 3.72 GPa @Strain 3.17 %, Temperature 40.0 °C |
539 ksi @Strain 3.17 %, Temperature 104 °F |
DAM; ISO 11403-1 -2 | |||
| 3.89 GPa @Strain 2.13 %, Temperature 23.0 °C |
564 ksi @Strain 2.13 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |||
| 4.40 GPa @Strain 0.630 %, Temperature 40.0 °C |
638 ksi @Strain 0.630 %, Temperature 104 °F |
50%RH; ISO 11403-1 -2 | |||
| 5.66 GPa @Strain 0.570 %, Temperature 23.0 °C |
821 ksi @Strain 0.570 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |||
| 5.8051 GPa @Strain 1.57 %, Temperature 40.0 °C |
841.97 ksi @Strain 1.57 %, Temperature 104 °F |
DAM; ISO 11403-1 -2 | |||
| 7.5175 GPa @Strain 0.400 %, Temperature 40.0 °C |
1090.3 ksi @Strain 0.400 %, Temperature 104 °F |
DAM; ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 50%RH; ISO 180/1A | ||
| 21.0 kJ/m² | 9.99 ft-lb/in² | DAM; ISO 180/1A | |||
| 10.0 kJ/m² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
50%RH; ISO 180/1A | |||
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 180/1A | |||
| 14.0 kJ/m² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 180/1A | |||
| 15.0 kJ/m² @Temperature -40.0 °C |
7.14 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 74.0 kJ/m² | 35.2 ft-lb/in² | DAM; ISO 180/1U | ||
| 80.0 kJ/m² | 38.1 ft-lb/in² | 50%RH; ISO 180/1U | |||
| 75.0 kJ/m² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 180/1U | |||
| 80.0 kJ/m² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 180/1U | |||
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | 50%RH; ISO 179/1eU | ||
| 9.10 J/cm² | 43.3 ft-lb/in² | DAM; ISO 179/1eU | |||
| 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |||
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | DAM; ISO 179/1eA | ||
| 2.20 J/cm² | 10.5 ft-lb/in² | 50%RH; ISO 179/1eA | |||
| 1.30 J/cm² @Temperature -40.0 °C |
6.19 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA | |||
| 1.30 J/cm² @Temperature -40.0 °C |
6.19 ft-lb/in² @Temperature -40.0 °F |
50%RH; ISO 179/1eA | |||
| 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V | 600 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C | 8.33 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 119 µm/m-°C | 66.1 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| 95.0 µm/m-°C @Temperature -40.0 °C |
52.8 µin/in-°F @Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 95.0 µm/m-°C @Temperature 23.0 °C |
52.8 µin/in-°F @Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 95.0 µm/m-°C @Temperature 95.0 °C |
52.8 µin/in-°F @Temperature 203 °F |
ISO 11403-1 -2 | |||
| Specific Heat Capacity | 2.20 J/g-°C | 0.526 BTU/lb-°F | |||
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 262 °C | 504 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | DAM; ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | ||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
DAM; IEC 60695-11-10 | |||
| Oxygen Index | 23 % | 23 % | DAM; ISO 4589-1/-2 | ||
| De |
|||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PA66-IGF33< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA66-IGF33 | ||||
| UL recognition | UL | DAM | |||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。
上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！
可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：
联系人：邓小姐
联系电话：13917657923
联系QQ:996152797
联系邮箱：996152797@qq.com