| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.870 g/cc | 0.0314 lb/in³ | |||
| 1.02 g/cc | 0.0368 lb/in³ | DAM; ISO 1183 | |||
| Viscosity | 57470 cP @Shear Rate 5000 1/s, Temperature 280 °C |
57470 cP @Shear Rate 5000 1/s, Temperature 536 °F |
ISO 11403-1 -2 | ||
| 81230 cP @Shear Rate 5000 1/s, Temperature 245 °C |
81230 cP @Shear Rate 5000 1/s, Temperature 473 °F |
ISO 11403-1 -2 | |||
| 96410 cP @Shear Rate 5000 1/s, Temperature 230 °C |
96410 cP @Shear Rate 5000 1/s, Temperature 446 °F |
ISO 11403-1 -2 | |||
| 213500 cP @Shear Rate 500 1/s, Temperature 280 °C |
213500 cP @Shear Rate 500 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| 370500 cP @Shear Rate 500 1/s, Temperature 245 °C |
370500 cP @Shear Rate 500 1/s, Temperature 473 °F |
ISO 11403-1 -2 | |||
| 465400 cP @Shear Rate 500 1/s, Temperature 230 °C |
465400 cP @Shear Rate 500 1/s, Temperature 446 °F |
ISO 11403-1 -2 | |||
| Viscosity Test | 55 cm³/g | 55 cm³/g | DAM; ISO 307 1157 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 30.0 MPa @Strain 50.0 % |
4350 psi @Strain 50.0 % |
DAM; ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | DAM; ISO 527-1/-2 | ||
| Tensile Modulus | 0.900 GPa | 131 ksi | DAM; ISO 527-1/-2 | ||
| Flexural Modulus | 0.880 GPa | 128 ksi | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | NB | NB | DAM; ISO 180/1A | ||
| Charpy Impact, Notched | 13.5 J/cm² | 64.2 ft-lb/in² | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 2.70 J/g-°C | 0.645 BTU/lb-°F | |||
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 221 °C | 430 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | DAM; 10°C/min; ISO 11357-1/-2 | ||
| De |
|||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PA6-F< | ISO 11469 | |||
| Processing | Blow Moulding | ||||
| Coatable | |||||
| Film Extrusion | |||||
| Injection Moulding | |||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Sheet Extrusion | |||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA6-F | ||||
| PA6-F | ISO 1043 | ||||
| Special characteristics | Heat stabilised or stable to heat | ||||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。