| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | DAM; ASTM D792 | ||
| Density | 1.16 g/cc | 0.0419 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 1.8 % @Temperature 23.0 °C |
1.8 % @Temperature 73.4 °F |
Immersion 24h; DAM; ISO 62, Similar to | ||
| Linear Mold Shrinkage | 0.0080 cm/cm @Thickness 1.60 mm |
0.0080 in/in @Thickness 0.0630 in |
Flow; DAM | ||
| 0.0080 cm/cm @Thickness 1.60 mm |
0.0080 in/in @Thickness 0.0630 in |
Transverse; DAM | |||
| 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
Flow; DAM | |||
| 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
Transverse; DAM | |||
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 2.00 mm |
0.0090 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm |
0.010 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa @Temperature 23.0 °C |
11600 psi @Temperature 73.4 °F |
DAM; ISO 527 | ||
| Tensile Strength | 89.6 MPa @Temperature 23.0 °C |
13000 psi @Temperature 73.4 °F |
DAM; ASTM D638 | ||
| Tensile Strength, Yield | 90.0 MPa @Temperature 23.0 °C |
13100 psi @Temperature 73.4 °F |
50mm/min; DAM; ISO 527 | ||
| Elongation at Break | 10 % @Temperature 23.0 °C |
10 % @Temperature 73.4 °F |
DAM; nominal; ISO 527 | ||
| 10 % @Temperature 23.0 °C |
10 % @Temperature 73.4 °F |
DAM; ISO 527 | |||
| 14 % @Temperature 23.0 °C |
14 % @Temperature 73.4 °F |
DAM; ASTM D638 | |||
| Elongation at Yield | 4.0 % @Temperature 23.0 °C |
4.0 % @Temperature 73.4 °F |
50mm/min; DAM; ISO 527 | ||
| Tensile Modulus | 3.75 GPa @Temperature 23.0 °C |
544 ksi @Temperature 73.4 °F |
DAM; ISO 527 | ||
| Flexural Modulus | 3.45 GPa @Temperature 23.0 °C |
500 ksi @Temperature 73.4 °F |
DAM; ASTM D790 | ||
| 3.66 GPa @Temperature 23.0 °C |
531 ksi @Temperature 73.4 °F |
DAM; ISO 178 | |||
| Izod Impact, Notched | 0.430 J/cm @Temperature 23.0 °C |
0.806 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D256 | ||
| Charpy Impact Unnotched | 13.5 J/cm² @Temperature 23.0 °C |
64.2 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA | ||
| 0.370 J/cm² @Temperature 23.0 °C |
1.76 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | >= 600 V | >= 600 V | DAM; IEC 60112 | ||
| >= 600 V @Thickness 3.00 mm, Temperature 23.0 °C |
>= 600 V @Thickness 0.118 in, Temperature 73.4 °F |
DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 264 °C | 507 °F | DAM; ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | DAM; ASTM D648 | ||
| 235 °C | 455 °F | DAM; ISO 75-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ASTM D648 | ||
| 84.0 °C | 183 °F | DAM; ISO 75-1/-2 | |||
| UL RTI, Electrical | 130 °C @Thickness 1.50 mm |
266 °F @Thickness 0.0591 in |
DAM; UL 746B | ||
| 130 °C @Thickness 3.00 mm |
266 °F @Thickness 0.118 in |
DAM; UL 746B | |||
| 130 °C @Thickness 0.750 mm |
266 °F @Thickness 0.0295 in |
DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 0.750 mm |
167 °F @Thickness 0.0295 in |
DAM; UL 746B | ||
| 75.0 °C @Thickness 1.50 mm |
167 °F @Thickness 0.0591 in |
DAM; UL 746B | |||
| 75.0 °C @Thickness 3.00 mm |
167 °F @Thickness 0.118 in |
DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 85.0 °C @Thickness 0.750 mm |
185 °F @Thickness 0.0295 in |
DAM; UL 746B | ||
| 85.0 °C @Thickness 1.50 mm |
185 °F @Thickness 0.0591 in |
DAM; UL 746B | |||
| 85.0 °C @Thickness 3.00 mm |
185 °F @Thickness 0.118 in |
DAM; UL 746B | |||
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
DAM; IEC 60695-11-10 | ||
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
DAM; IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
DAM; UL94 | |||
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
DAM; UL94 | |||
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
DAM; UL94 | |||
| Glow Wire Test | 775 °C @Thickness 3.00 mm |
1430 °F @Thickness 0.118 in |
DAM; Ignition; IEC 60695-2-13 | ||
| 775 °C @Thickness 1.50 mm |
1430 °F @Thickness 0.0591 in |
DAM; Ignition; IEC 60695-2-13 | |||
| 960 °C @Thickness 1.50 mm |
1760 °F @Thickness 0.0591 in |
DAM; IEC 60695-2-12 | |||
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
DAM; IEC 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 °C | 536 °F | DAM; Optimum | ||
| 270 - 290 °C | 518 - 554 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| De |
|||||
| Additive | Flame Retardant | DAM | |||
| Lubricant | DAM | ||||
| Appearance | Natural Color | DAM | |||
| Contains Flame Retardant | Yes | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Crystalline, Semi | DAM | |||
| Flame Retardant | DAM | ||||
| Nucleated | DAM | ||||
| Processability, Good | DAM | ||||
| Flame Retardant - Halogen/Red Phosphorus Free | Yes | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-FR(30)< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Flame Retardant Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-FR(30) | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Connectors | DAM | |||
| Electrical Parts | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。