| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | DAM; ASTM D792 | ||
| Water Absorption | 0.98 % @Temperature 23.0 °C |
0.98 % @Temperature 73.4 °F |
Immersion 24h; DAM; ASTM D570 | ||
| Linear Mold Shrinkage | 0.015 cm/cm @Thickness 3.20 mm |
0.015 in/in @Thickness 0.126 in |
Transverse; DAM | ||
| 0.023 cm/cm @Thickness 3.20 mm |
0.023 in/in @Thickness 0.126 in |
Flow; DAM | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 70 | 70 | 50%RH; ASTM D785 | ||
| 106 | 106 | DAM; ASTM D785 | |||
| Tensile Strength | 43.4 MPa @Temperature 23.0 °C |
6290 psi @Temperature 73.4 °F |
50%RH; ASTM D638 | ||
| 52.4 MPa @Temperature 23.0 °C |
7600 psi @Temperature 73.4 °F |
DAM; ASTM D638 | |||
| Elongation at Break | 90 % @Temperature 23.0 °C |
90 % @Temperature 73.4 °F |
DAM; ASTM D638 | ||
| 200 % @Temperature 23.0 °C |
200 % @Temperature 73.4 °F |
50%RH; ASTM D638 | |||
| Flexural Modulus | 0.331 GPa @Temperature 100 °C |
48.0 ksi @Temperature 212 °F |
DAM; ASTM D790 | ||
| 0.897 GPa @Temperature 23.0 °C |
130 ksi @Temperature 73.4 °F |
50%RH; ASTM D790 | |||
| 1.862 GPa @Temperature 23.0 °C |
270.1 ksi @Temperature 73.4 °F |
DAM; ASTM D790 | |||
| Izod Impact, Notched | 10.62 J/cm @Temperature 23.0 °C |
19.90 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D256 | ||
| Izod Impact, Unnotched | 10.6 J/cm @Temperature 23.0 °C |
19.9 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D4812 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 260 °C | 500 °F | DAM; ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | DAM; ISO 75-1/-2 | ||
| 98.0 °C | 208 °F | DAM; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | DAM; ISO 75-1/-2 | ||
| 55.0 °C | 131 °F | DAM; ASTM D648 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum | ||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| De |
|||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Forms | Pellets | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Processing Method | Extrusion | DAM | |||
| Product Category | Extrusion Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Unreinforced Resins | DAM | ||||
| RoHS Compliance | Contact Manufacturer | DAM | |||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。